The matrix assisted pulsed laser evaporation (MAPLE) technique has been used for the deposition of metal dioxide (TiO₂, SnO₂) nanoparticle thin films for gas sensor applications. For this purpose, colloidal metal dioxide nanoparticles were diluted in volatile solvents, the solution was frozen at the liquid nitrogen temperature and irradiated with a pulsed excimer laser. The dioxide nanoparticles were deposited on Si and Al₂O₃ substrates. A rather uniform distribution of TiO₂ nanoparticles with an average size of about 10 nm and of SnO₂ nanoparticles with an average size of about 3 nm was obtained, as demonstrated by high resolution scanning electron microscopy (SEM-FEG) inspections. Gas-sensing devices based on the resistive transduction mechanism were fabricated by depositing the nanoparticle thin films onto suitable rough alumina substrates equipped with interdigitated electrical contacts and heating elements. Electrical characterization measurements were carried out in controlled environment. The results of the gas-sensing tests towards low concentrations of ethanol and acetone vapors are reported. Typical gas sensor parameters (gas responses, response/recovery time, sensitivity, and low detection limit) towards ethanol and acetone are presented.

A poly-(3-hexylthiophene) (P3HT)/[6,6]-phenyl-C₆₁-butyric-acid-methyl-ester (PCBM) bilayer structure has been realized by single step matrix-assisted pulsed laser evaporation (ss-MAPLE) technique using the same solvent for both the polymers under vacuum conditions. Our ss-MAPLE procedure allows the fabrication of polymeric multilayer device stacks, which are very difficult to realize with the conventional solvent assisted deposition methods. A proof of concept bilayer P3HT/PCBM solar cell based on ss-MAPLE deposition has been realized and characterized. This demonstration qualifies ss-MAPLE as a general and alternative technique for the implementation of polymeric materials in hetero-structure device technology.

The sensing performance comparisons presented in this work were carried out by exploiting a suitable magneto-plasmonic sensor in both the traditional surface plasmon resonance configuration and the innovative magneto-optic surface plasmon resonance one. The particular multilayer transducer was functionalized with TiO₂ Brookite nanorods layers deposited by matrix assisted pulsed laser evaporation, and its sensing capabilities were monitored in a controlled atmosphere towards different concentrations of volatile organic compounds mixed in dry air.