Ultralow friction polymer composites were prepared by adding oil-loaded microcapsules into epoxy (EP) resin. Mono-dispersed polystyrene (PS)/poly alpha olefin (PAO) microcapsules with a diameter of ~2 μm and a shell thickness of ~ 30 nm were prepared by solvent evaporation method in an oil-in-water emulsion. The lubrication behaviors of the EP resin composites with oil-loaded microcapsules have been investigated under different loads and sliding speeds. As compared with the pure EP resin, the friction coefficient of the composite could be reduced to 4% (from 0.71 to 0.028) and the wear rate could be decreased up to two orders of magnitude. It was demonstrated that the released PAO oil from the microcapsules during the friction process produced a boundary lubricating film, which could prevent the direct contact of two rubbing surfaces, and thus leading to an extremely low friction coefficient and wear rate. Moreover, the composites with microcapsules could achieve comparable lubrication properties to the case under the external lubrication condition, while the former case could effectively minimize the lubricant leakage and improve the lubrication efficiency.

Developing green, environmental, sustainable new energy sources is an important problem to be solved in the world. Among the new energy technologies, water splitting system, fuel cell technology and metal-air battery technology are the main energy production and conversion methods, which involve three main electrocatalytic reactions, hydrogen evolution reaction (HER), oxygen evolution reaction (OER), and oxygen reduction reaction (ORR). The efficiency of the electrocatalytic reaction and the power consumption are very dependent on the activity of the electrocatalysts. Among various electrocatalysts, the two-dimensional (2D) materials have received widespread attention due to multiple advantages, such as their easy availability and low price. What' important is that they have adjustable physical and chemical properties. It is possible to develop them as electrocatalysts to replace the noble metals. Therefore, the design of two-dimensional electrocatalysts is a focus in the research area. Some recent advances in ultrasound-assisted preparation of two-dimensional (2D) materials have been overviewed according to the kind of materials in this review. Firstly, the effect of the ultrasonic cavitation and its applications in the synthesis of inorganic materials are introduced. The ultrasonic-assisted synthesis of representative 2D materials for example transition metal dichalcogenides (TMDs), graphene, layered double metal hydroxide (LDH), and MXene, and their catalytic properties as electrocatalysts are discussed in detail. For example, the CoMoS₄ electrocatalysts have been synthesized through a facile ultrasound-assisted hydrothermal method. The obatined HER and OER overpotential of CoMoS₄ electrode is 141 and 250 mV, respectively. This review points out some problems that need to be solved urgently at present, and provides some ideas for designing and constructing two-dimensional materials with better electrocatalytic performance.