Graphene oxide (GO) has attracted significant attention as a nano-reinforcement for cement-based materials, owing to its exceptional mechanical properties and abundant surface functional groups. However, the precise mechanisms governing its effects in cement composites remain inadequately understood due to inconsistencies and gaps in the existing literature. This review conducts a comprehensive analysis of the dispersion and reinforcement effects of GO in cement materials, focusing on three key areas: (1) challenges associated with achieving uniform dispersion of GO in the high-pH environment of cement slurries and potential strategies to address them; (2) the influence of GO on the macroscopic properties of cementitious composites, including workability, load-bearing capacity, flexural strength, fracture resistance, and durability; and (3) the reinforcement mechanisms of GO, encompassing its role in hydration kinetics, alterations to the calcium-silicate-hydrate (C-S-H) structure, and bonding interactions at the cement matrix interface. Furthermore, recent advancements in optimizing the dispersion and reinforcement effects of GO, such as surface modification techniques, are explored, emphasizing its potential for multifunctional and intelligent applications. This review aims to provide engineering professionals with the latest insights into the application of graphene oxide as a nano-reinforcement in cement-based composites, while offering valuable guidance and direction for future research in this field.

Wasted concrete was often used as a recycled aggregate instead natural stone in fresh concrete to reduce the environmental impact in a decade. However, because of the residual mortar interface, the performance of recycled aggregate was weaker. In this paper, the recycled aggregate was prewetted, and the effects of prewetted degree on the workability, strength, and durability of concrete were studied. The properties of the interfacial transition zone (ITZ), including microhardness, pore structure, and width, were also investigated. The results show that the workability intensity increased with the increase in prewetted degree from 0% to 100%, while the strength was first increased and then decreased with the optimal value of 43.3 MPa when the prewetted degree was 50–65%. The water absorption and chloride ion diffusion coefficient were also decreased by approximately 10% at minimum with the prewetted degree around 55% because of the declined fraction of pores larger than 50 μm and smaller porosity. The width of ITZ was first sharply decreased with a prewetted degree of 50–65%, then increased again with higher moisture, while microhardness of the ITZ showed the opposite trend and reached 82.7 MPa at maximum, at 50%. The appropriate moisture (50–65%) improved the pore structure and hydration products with an internal curing effect. When the moisture content was too high, the excess water was released from aggregate to the matrix, causing a higher water–cement ratio at ITZ; the porosity and the number of macrospores were increased to weaken the performance of concrete.

An efficient electrocatalyst of CuCo₂S₄@CoS₂ using ZIF-67 as a template was synthesized. The interconnected structure, high conductivity, and interfacial interactions endow the catalyst with enhanced HER, OER, and overall water splitting activity.