Dyes used by the textile, tannery, and food industries tend to pollute water bodies and must be removed to get clean water. Hydroxyapatite (HAP) was synthesized from eggshells using the wet precipitation process. The as-synthesized HAP was characterized using Fourier Transform Infrared (FTIR) and X-ray powder diffraction (XRD). The synthesized HAP was mixed with three different clays: halloysite (HNT), kaolinite (KAO), and bentonite (BENT). The removal efficiency values of methylene blue (MB) from the data showed that HAP-BENT adsorbents had higher values, followed by HAP-HNT and then HAP-KAO adsorbents. The combined masses of 24 mg, 34.5 mg, and 33 mg (representing 20%, 15%, and 10% of HAP-BENT mass) had average adsorption capacity values of 20.7 mg/g, 17.2 mg/g, and 17.9 mg/g, respectively. For each mass percentage, the adsorption capacity values were found to decrease with adsorbent dosage. The HAP-BENT composites had removal efficiency values of 98.4, 91.9%, and 91.9%, respectively. Adsorption data for the HAP-BENT adsorbents were found to be well described by the Langmuir isotherm model and pseudo-second-order kinetic model. The effect of temperature on adsorption capacity was evaluated and thermodynamical modeling was undertaken. The thermodynamical modeling predicts that based on the value of the change in enthalpy and Gibbs free energy the process was exothermic and spontaneous. This work confirms the potential of HAP-clay composites in removing MB from water.

The composites of properties of ethylene-propylene-diene-monomer (E) and acrylonitrile butadiene-rubber (N) composites of graphene oxide (GO) and reduced graphene oxide (G) were prepared by a combination of solution and open-roll method. They include single matrices (EGO and EG) and blends N/E, 20 part of hundreds of rubber (phr)/80 phr (A), 80 phr/20 phr (B), and 50 phr/50 phr(C) blend containing GO and G. The physico-mechanical properties including vulcanization, tensile, glass transition temperature (), and dielectric spectroscopic properties were evaluated. The N-rich systems reinforced with GO, cured faster than the E-rich systems. Also, N-rich systems obtained the highest dielectric constant , especially when GO and G were incorporated, for example, NG and N-GO obtained 317 and 283% increment in than EG and EGO, respectively. In terms of tensile properties, AGO exhibited the highest strength and elongation at break properties (%). Therefore, solution mixing technique of rubber blends filled with nanoinclusion can be achieved with the tendency of reducing cost without the use of compatibilizer and still maintain the integrity of the physical properties of the final product. The result obtained therefore shows that the current compositions can find various applications in oil/gas sealants, heat-resistant applications, and energy storage materials with minimal losses.

Ethylene-propylene grafted-maleic anhydride (EPR-g-MA) and a pure maleic anhydride (MA) were separately used to compound carboxylated acrylonitrile butadiene-rubber (XNBR) together with reduced graphene oxide (G) to form nanocomposites, by using melt compounding technique. The G-sheets in the presence of MA (GA samples) or EPR-g-MA (GB samples) generally increased the physico-mechanical properties including; crosslinking density, tensile strength and thermal degradation resistance etc., when compared with sample without MA or EPR-g-MA (GAO) and the virgin matrix. For the thermal degradation resistance measured by the char residue (%), by using thermal gravimetric analysis technique; GA1 (0.1 ph G and 0.5 ph MA) was 106.4% > XNBR and 58% > GAO (0.1 ph G) while that of GB1 (0.1 ph G and 0.5 ph EPR-g-MA) was 60% > XNBR and 22.2% > GAO respectively. Although, homogeneous dispersions of the G-sheets assisted by MA or EPR-g-MA was a factor, but the strong bonding (covalent, hydrogen and physical entanglements) occurring in GA and GB was observed to be the main contributing factor for these property enhancements. Thus, these nanostructured materials have exhibited multifunctional capabilities and could be used for advanced applications including high temperature (heat sinks), flame retardants, and structural applications.