Background: So far, the effect of graphene oxide (GO) and reduced graphene oxide (rGO) in rubber matrix has not been well established. Methods: The effects of graphene oxide (GO) and reduced graphene oxide (rGO) on the physical properties of polar acrylonitrile-butadiene rubber (NBR) and non-polar Ethylene-propylene-diene terpolymer rubber (EPDM) matrix have been investigated and their properties compared. NBR vulcanizates exhibited higher cure rates compared to the EPDM systems. Results: Effective dispersion of the nanosheets within the different matrices was observed to be a reason for the improvement in properties, but the effective nanosheets-matrix interactions played a key role in reinforcing action. This was noticeable in the various properties (crosslinking density, tensile properties, and dynamical mechanical analysis) evaluated. Typically, the polar NBR matrix was observed to show about 461 and 405% higher interactions parameter with GO and rGO fillers (loaded from 0.1~1phr) than composites of EPDM based on Kraus model. Conclusions: While this present work has confirmed the significance of considering the polarities of graphene sheets or derivative graphene (GSD) and their respective polymers matrices for effective property enhancement for specific applications, it has also demonstrated the future prospects of rubber-graphene nanocomposites for several applications which include structural, barrier, and dielectric energy storage materials.

The composites of properties of ethylene-propylene-diene-monomer (E) and acrylonitrile butadiene-rubber (N) composites of graphene oxide (GO) and reduced graphene oxide (G) were prepared by a combination of solution and open-roll method. They include single matrices (EGO and EG) and blends N/E, 20 part of hundreds of rubber (phr)/80 phr (A), 80 phr/20 phr (B), and 50 phr/50 phr(C) blend containing GO and G. The physico-mechanical properties including vulcanization, tensile, glass transition temperature (), and dielectric spectroscopic properties were evaluated. The N-rich systems reinforced with GO, cured faster than the E-rich systems. Also, N-rich systems obtained the highest dielectric constant , especially when GO and G were incorporated, for example, NG and N-GO obtained 317 and 283% increment in than EG and EGO, respectively. In terms of tensile properties, AGO exhibited the highest strength and elongation at break properties (%). Therefore, solution mixing technique of rubber blends filled with nanoinclusion can be achieved with the tendency of reducing cost without the use of compatibilizer and still maintain the integrity of the physical properties of the final product. The result obtained therefore shows that the current compositions can find various applications in oil/gas sealants, heat-resistant applications, and energy storage materials with minimal losses.