This paper proposes a new damage index named degree of health (DoH) to efficiently tackle structural damage monitoring in real-time. As a key contribution, the proposed index relies on a pattern matching methodology that measures the time-of-flight mismatch of sequential ultrasonic guided-wave measurements using fuzzy logic fundamentals. The ultrasonic signals are generated using the transmission beamforming technique with a phased-array of piezoelectric transducers. The acquisition is carried out by two phased-arrays to compare the influence of pulse-echo and pitch-catch modes in the damage assessment. The proposed monitoring approach is illustrated in a fatigue test of an aluminum sheet with an initial notch. As an additional novelty, the proposed pattern matching methodology uses the data stemming from the transmission beamforming technique for structural health monitoring. The results demonstrate the efficiency and robustness of the proposed framework in providing a qualitative and quantitative assessment for fatigue crack damage.

Multimaterial solutions that combine adhesively bonded composite and metallic parts are being widely proposed as lightweighting strategies to reduce environmental impact. However, the introduction of adhesive interphases in components subjected to fatigue loads is a major concern in terms of durability, reliability and maintainability. Structural health monitoring (SHM) techniques can play a key role in providing structures with self‐sensing capabilities. Although the use of ultrasonic guided wave (UGW) monitoring for predicting the damage of in‐service adhesive joints has been proved feasible, several challenges remain, including the generation of large and high‐quality data sets and the scalability of damage detection algorithms for real‐world use cases. After a wide literature review of available algorithms and simulation techniques, the simplest yet accurate methods have been selected to build a methodology that may eventually be fostered with more complex models. In this work, a numerical–experimental integrative methodology is proposed to train predictive algorithms minimizing the need for extensive experimental campaigns, by creating synthetic data sets through physics‐based simulation models. Although several features have been detected as damage‐sensitive, simple regression models using the root‐mean‐square density (RMSD) have been trained and validated as damage indicators. The feasibility of this approach has been proven in a real subcomponent with an error below 2% in the debonding length prediction, calculated as the ratio of the Euclidean distance between actual debonding and predicted debonding to the total inspection length.

In this paper, we introduce an advanced AI-based solution for predicting structural damage in aircraft laminates. Our innovative approach focuses on detecting and locating fatigue damage within composite structures, thereby enhancing the assessment of aircraft health and usage. By leveraging state-of-the-art ultrasonic guided wave (UGW) inspection simulations of composite laminates integrated with piezoelectric transducers, comprehensive datasets are extracted efficiently. The signals captured by the piezoelectric sensors are utilized to engineer key features sensitive to composite structural damage, which are then used to train a deep neural network (DNN) for accurate structural damage prediction. Our findings demonstrate the significant potential of combining advanced simulation techniques with machine learning to improve the accuracy and reliability of structural health monitoring in aerospace applications.

This work addresses a critical challenge for the implementation of Structural Health Monitoring (SHM) systems in the aerospace sector: the validation of Ultrasonic Guided Wave (UGW) models in curved geometries and under real conditions of fatigue crack growth. The geometric complexity of curved aeronautical composites generates dispersion, attenuation, and mode conversion that complicates UGW signal interpretation. While UGW monitoring is well-established for flat composites and fatigue damage is more commonly tracked via Acoustic Emission (AE), validated models for mixed-mode fatigue delamination in curved components remain scarce. The main objective is to validate a 2D Finite Element Model (FE) developed at Abaqus to simulate the precise interaction between guided waves (A0 and S0 modes) and a Mixed-Mode fatigue delamination in two curved specimens of different materials and thicknesses. A co-simulation model was implemented to replicate the Round-Robin tests with Macro Fiber Composite (MFC) transducers, in which crack propagation was experimentally monitored using UGW through two bonded MFC piezoelectric sensors acting as both actuators and receivers, while a 15 mm PTFE film was inserted during manufacturing to ensure crack growth in a single delamination plane. The delamination simulation was carried out by progressively releasing the nodes of the set of contact nodes between the upper and lower surfaces of the delamination, resulting in a free surface, replicating the Severity and Location of the Damage (SoD and LoD) observed experimentally. Numerical-experimental validation focused on comparing the trends of the same key signal features extracted from the experimental campaign and the FE simulations as the material was damaged. The results confirm a high correlation in the features, demonstrating that the FE model successfully captures the effect of delamination growth and wave-curvature interaction. Finally, this validated model is proposed as the ideal training environment for a Leave-One-Group-Out Cross Validation (LOGO-CV) scheme for material generalization, demonstrating robustness to manufacturing variations.

The safety and service life of next-generation aerospace composite structures depend on the integrity of their complex geometries, such as curved C-sections. This paper presents a comprehensive methodology for Structural Health Monitoring (SHM) focused on the study of Mixed-Mode fracture in two curved composite demonstrators. The main objective is to develop and validate a Digital Twin (DT) framework capable of predicting the growth of delamination in real time under operational loads. The approach is to establish an accurate correlation between the Ultrasonic Guided Wave (UGW) data captured in-situ during fracture tests and the delamination status predicted by high-fidelity numerical models. This correlation is essential for an effective transition from traditional non-destructive testing (NDT) methods to intelligent SHM systems. The methodology is based on the continuous acquisition of UGW signals using a Micro-Fiber Composite (MFC) sensor network. Key UGW signal features are then extracted to estimate the experimental delamination size, which growth is correlated with Finite Element (FE) simulations and Reduced Order Models (ROMs), creating a direct mapping between the experimental features of the UGW signals and the numerical delamination progression. This validated Digital Twin allows the SHM system to use real-time UGW data to estimate remaining life and structural integrity under future load scenarios. In essence, the validation demonstrates the feasibility of an active UGW-based SHM system for continuous monitoring of Mixed-Mode fractures. This methodology, developed within the framework of the Horizon European GENEX Project, represents a significant step towards autonomous maintenance strategies for composite aircraft, improving safety margins and reducing inspection downtime.

Carbon-fibre reinforced polymer (CFRP) laminates are susceptible to both static and fatigue-driven delamination. Predicting this type of failure in curved composite structures, often referred to as delamination by unfolding, remains a critical challenge. This work presents the development of a Virtual Crack Closure Technique (VCCT)-based computational method for simulating fatigue-driven delamination propagation under non-constant mixed-mode conditions. The fatigue delamination growth model follows a phenomenological approach based on a Paris–Erdogan-based power-law relationship, where the delamination propagation rate depends on the strain energy release rate. This methodology has been implemented as a user-defined subroutine, UMIXMODEFATIGUE, for Abaqus, integrating the effects of load ratio and mode mixity conditions while leveraging the mode separation provided by VCCT. The proposed approach is validated against an experimental case involving a four-point bending test applied to an L-shaped CFRP curved beam specimen with a unidirectional layup. Unlike the existing standard configuration, the proposed test campaign introduces a non-adhesive Teflon foil insert at the bend, placed within the midplane layers to act as a delamination initiator, representing a manufacturing defect. In addition to the testing machine, digital image correlation (DIC) is used to monitor delamination length. The simulation method developed accurately predicts fatigue delamination propagation under varying mode mixity at the delamination front. By improving delamination modelling in composites, this approach supports timely maintenance and helps prevent fatigue failures. Additionally, it deepens the understanding of how the mode mixity influences the delamination propagation process.