Composite laminates experience static and fatigue delamination, presenting significant challenges for failure prediction. This is critical in curved composites, where delamination behavior is complex to predict. In this study, fatigue tests were conducted on curved composite laminates under non-constant mixed-mode conditions. The testing setup involved a four-point bending test using L-shaped, unidirectional carbon-fiber-reinforced polymer curved beam specimens. A Teflon insert placed at the bend was used to initiate delamination. Experimental data acquisition included digital image correlation (DIC) to monitor delamination length during testing. This is important since it enhances subsequent model correlation. A virtual crack closure technique (VCCT)-based method for simulating fatigue-driven delamination under variable mixed-mode conditions was validated against experiments. Delamination growth was modeled using a Paris-like power–law relationship based on the strain energy release rate. The approach was implemented in Abaqus as a user subroutine, incorporating load ratio and mode mixity effects through VCCT-based mode separation. This study demonstrates accurate fatigue delamination prediction and highlights the role of optical measurements in experiments. The model improves our understanding of delamination propagation under varying mode mixity and contributes to structural integrity analysis. The results show how mode mixity influences delamination, impacting the performance and lifecycle of composite structures.

Carbon-fibre reinforced polymer (CFRP) laminates are susceptible to both static and fatigue-driven delamination. Predicting this type of failure in curved composite structures, often referred to as delamination by unfolding, remains a critical challenge. This work presents the development of a Virtual Crack Closure Technique (VCCT)-based computational method for simulating fatigue-driven delamination propagation under non-constant mixed-mode conditions. The fatigue delamination growth model follows a phenomenological approach based on a Paris–Erdogan-based power-law relationship, where the delamination propagation rate depends on the strain energy release rate. This methodology has been implemented as a user-defined subroutine, UMIXMODEFATIGUE, for Abaqus, integrating the effects of load ratio and mode mixity conditions while leveraging the mode separation provided by VCCT. The proposed approach is validated against an experimental case involving a four-point bending test applied to an L-shaped CFRP curved beam specimen with a unidirectional layup. Unlike the existing standard configuration, the proposed test campaign introduces a non-adhesive Teflon foil insert at the bend, placed within the midplane layers to act as a delamination initiator, representing a manufacturing defect. In addition to the testing machine, digital image correlation (DIC) is used to monitor delamination length. The simulation method developed accurately predicts fatigue delamination propagation under varying mode mixity at the delamination front. By improving delamination modelling in composites, this approach supports timely maintenance and helps prevent fatigue failures. Additionally, it deepens the understanding of how the mode mixity influences the delamination propagation process.