The aim of this study is to investigate the oxalic acid activation of bentonites containing different types of smectites, analyse their surface modification as a function of acid concentration and create good quality bleaching earths. In particular, two different bentonite samples (one containing aluminum and one containing ferruginous smectite), after being characterized through XRD, XRF and FT-IR analysis, are treated with oxalic acid at a concentration of 0.5, 0.7 and 1 M. Their structural modifications after treatment are observed through FT-IR spectra and surface area and porosity measurement (using the BET equation and the BJH method, respectively) combined with the determination of the main structural metals’ extraction from them (using an atomic adsorption spectrometer). The results showed that the ferruginous smectite is more susceptible to oxalic acid activation compared to the aluminum smectite, and all the final products have developed extra porosity in their structure while retaining the structure of smectite (even at 0.5 M acid concentration). The activated samples were used as bleaching earths in soybean oil, and the results proved that Lovibond yellow and red colours as well as the chlorophyll of oil (measured spectrophotometrically) were reduced to the values set by the specifications.

The conventional lithium extraction method involves the calcination of a-spodumene at 1050 °C so that it can be converted to the more-reactive b-spodumene and then a sulfuric acid roasting step at 250 °C. Lithium is finally extracted via leaching with water. This method is energy-intensive, leading to high capital and operational costs. In this study, the direct calcination of a-spodumene with the use of sodium carbonate and calcium oxide was examined, aiming to significantly reduce the calcination temperature and completely omit the sulfuric acid roasting step, thereby radically redesigning the lithium extraction process. The calcination product was then leached with different leaching agents, such as water and sulfuric acid, and at different temperatures. The efficiency of the additives was evaluated through the results of lithium extraction achieved during the leaching step. Different leaching agents and temperatures were investigated. The maximum lithium extraction achieved was 96%, obtained after calcination using a sodium carbonate/spodumene mixture and leaching with sulfuric acid at 90 °C. High lithium extractions, up to 83%, can also be achieved under the same calcination conditions and after leaching with sulfuric acid at lower temperatures, such as 40 °C, and for shorter leaching times.

The present study aims to create porous materials through the acid activation of bentonites using 0.5 M oxalic acid at different pH values. Two types of bentonites (containing aluminum montmorillonite and ferruginous montmorillonite) were treated with oxalate solutions at pH 1 to 5. During acid activation at the three pH values, Al, Fe, Mg and Si kinetics were monitored; the porosity of the samples was modified; and the specific surface area increased, while the crystal structure did not completely collapse. The optimum conditions occurred at pH 1, where the highest metal leaching was obtained for both samples. For the sample with aluminum smectite, the specific surface increased from 28.1 m²/g to 149 m²/g and the pore volume quadrupled. In the case of samples with ferruginous smectite, the specific surface area rose from 63. 2 m²/g to 372 m²/g and the pore volume increased sixfold. The mechanism of smectite activation was investigated, revealing that at the optimum experimental conditions, which is ferruginous bentonite activation at pH 1, the products have the highest concentration of small 30 to 50 Å pores, which is attributed to the creation of an adequate number of active sites and the formation of aluminum complexes with the oxalate anions. The modified bentonites have elevated porosity; therefore, they could be used as adsorbents in industry.

Acid activation is a chemical modification of minerals and mainly smectites, in order to enhance their surface properties and reinforce their adsorption capacity for specific ions. Acid-activated clays and, more specifically, inorganic acid-activated calcium montmorillonites are mainly used in the bleaching process of vegetable oils, which are holding third place in the world food consumption after cereals and rice, in order to remove chlorophyll and other undesirable substances from the oils. This study proposes the use of oxalic acid for the acid activation of smectites, in order to modify their surface characteristics and create high-quality bleaching earths. In particular, aluminium and ferruginous smectites are treated with oxalic acid concentrations of 0.5, 0.7 and 1 M, and the structural modifications in the materials after treatment are observed through FTIR analysis, combined with the determination of the main structural metals’ extraction from the smectites. The results showed that ferruginous smectite is more susceptible to oxalic acid activation. The final product has developed vacant spaces in its structure to absorb other ions or molecules, although it retains the structure of smectite. Oxalic acid concentration of 0.5 M is sufficient for achieving this result. The materials produced through the oxalic acid activation are also compared with inorganic acid-activated smectites originating from the same deposits.