Key words: Dental marginal adaptation; Ceramics; Composite resins

To investigate the effect of resin cements on the color stability and translucency of ceramic laminate veneers used for diastema closure. Sixty resin abutments were prepared for ceramic laminate veneers and divided into six groups according to the ceramic type (lithium disilicate, zirconia-reinforced lithium silicate, and translucent zirconia) and the cement type (Variolink Esthetic LC and RelyX Veneer). Color coordinates and translucency were analyzed after cementation and after soaking in the coffee solution. Differences in color and translucency were estimated, and results were statistically assessed (α = 0.05). Ceramic materials showed a significant impact on color changes after soaking in coffee within Variolink Esthetic groups. Translucent zirconia showed the highest color change, followed by zirconia reinforced lithium silicate and lithium disilicate. Ceramic materials showed a significant impact among the RelyX Veneer groups. A significant interaction in color changes was found between ceramic types and cement types after cementation, and after soaking in coffee was found. All groups showed a clinically acceptable difference in translucency parameters after soaking in coffee. The resin cement affects the color and translucency of ceramic laminate veneers used for diastema closure, and ceramic laminate veneers bonded with Variolink Esthetic LC resin cement are more translucent, while ceramic laminate veneers bonded with RelyX Veneer resin are more resistant to coffee staining. The lithium disilicate laminate veneer is more resistant to coffee staining than zirconia reinforced lithium silicate and translucent zirconia laminate veneers used for diastema closure.

Objectives: Successful ceramic restorations depend on the strong bonding with resin cement and even stress distribution. The aim of this study was to evaluate the impact of adding MDP-containing zirconia primer before self-adhesive resin cements with different functional acidic monomers on fracture resistance of monolithic zirconia crown. Materials and methods: Eighty defect-free human maxillary premolars were divided according to the cement type and application of MDP-containing zirconia primer into eight groups (n = 10): Calibra Universal (C), Calibra Universal combined with zirconia primer (CZ), RelyX U200 (R), RelyXU200 combined with zirconia primer (RZ), Panavia SA Cement Plus (P), Panavia SA Cement Plus combined with zirconia primer (PZ), Multilink Speed (M), and Multilink Speed combined with zirconia primer (MZ). After teeth preparation and fabrication of zirconia crowns, each crown was bonded to its corresponding tooth. All specimens were subjected to 10,000 thermocycles between 5 and 55°C, followed by cyclic load (50 N) for 240,000 cycles. Each specimen was subjected to a static axial load until fracture using universal testing machine and the fracture load was recorded. The fracture mode studied and recorded. The fracture load results were analyzed using two-way ANOVA test (α = 0.05). Results: A significant interaction (P = 0.038) of combining MDP-containing zirconia primer and cement type on fracture resistance of monolithic zirconia crown was detected. The mean fracture load values of zirconia crown were significantly influenced by the combined application of the MDP-containing zirconia primer with Calibra Universal (P = 0.01), RelyX U200 (P < 0.001), and Multilink Speed (P = 0.038), while there was no significant difference with Panavia SA Cement Plus (P = 0.660). There was significant difference (F = 20.69, P < 0.001) between the mean fracture loads of groups with self-adhesive cements (C, R, P, and M groups). The highest fracture load was recorded with RZ group (2446.90 ± 126.72 N) while the lowest fracture load was recorded with C group (1623.18 ± 149.86 N). Conclusions: The self-adhesive resin cement with different acidic functional monomer affects the fracture resistance of monolithic zirconia crown. Application of MDP-containing primer could improve the fracture resistance of monolithic zirconia crown with most self-adhesive cements. The application of an MDP-containing primer had no impact on the fracture resistance of monolithic translucent zirconia crown bonded by MDP-containing self-adhesive resin cement.