Good cell adhesion is an important prerequisite for soft tissue attachment on implant abutment or crown surfaces. The aim of this study was to evaluate the adhesion and proliferation of human epithelial cells on sol-gel-derived TiO2-coated and noncoated zirconia. Altogether, 56 zirconia disks (Z-CAD, Metoxit) were fabricated for this study. Half of the disks were coated with a sol-gel-derived TiO2 coating (MetAlive, ID Creations). The rest of the disks were noncoated and formed the control group. Surface properties of the disks were characterized by contact angle measurements and surface free energy (SFE) calculation. The cell adhesion was tested by cultivating epithelial cells (20,000 cells/cm2) on the experimental disks for 1, 3, 6, and 24 hours, after which the fluorescence of the samples was measured (BioTek synergy HT). The amount of cells was detected by comparing the fluorescence value to the standard curve. In addition, the proliferation was studied by growing epithelial cells (25,000 cells/cm2) for 1, 3, and 7 days. The number of cells was calculated by defining the absorbance of the samples (Multiskan EX, Thermo Labsystems), followed by a comparison with the standard curve. Finally, the samples were processed for light microscopy. TiO2-coated disks were significantly more hydrophilic with higher total SFE than noncoated disks (P < .05). The amount of epithelial cells was greater on TiO2-coated disks than on controls after 24 hours (P < .05). Regarding cell proliferation, the difference was statistically significant (P < .05) on days 3 and 7. Light microscope evaluation confirmed viable cells, which were in immediate close contact with both substrate surfaces. The cell layers on the coated disks appeared to be more uniform and cell rich than the layers on noncoated disks. This study indicated that TiO2 coating improves epithelial cell attachment and proliferation on zirconia surfaces. This has good potential to enhance formation of the epithelial junction to the coated zirconia surfaces.

This in vitro study was designed to evaluate the effect of sol-gel derived TiO₂coating on blood coagulation, blood protein adsorption, and platelet response on zirconia surfaces. Square-shaped zirconia (n=96) (10x10x2 mm) was cut, ground, sintered, and finally cleansed ultrasonically in each of acetone and ethanol for 5 minutes. Three experimental groups (n=32) were fabricated: (a) zirconia coated with sol-gel derived TiO₂, (b) zirconia coated with sol-gel derived TiO₂and treated with ultraviolet (UV) irradiation for 1 hour, and (c) non-coated zirconia as control. The coatings were prepared from tetraisopropyl orthotitanate solution by dip-coating. The thrombogenicity of the specimens was evaluated using a whole blood kinetic clotting time method where the extent of blood clotting was evaluated at 10, 20, 30, 40, 50, and 60 minutes (n=4/time point, total n=24/group). Scanning electron microscope images were taken to observe platelet morphologies after 1-hour incubation with platelet-rich plasma (PRP) (n=5/group). Surface characteristics were visualized using atomic force microscopy (n=1/group). Adsorption of plasma proteins and fibronectin on each surface was studied by gel electrophoresis (n=2/group). Significant differences were observed in blood coagulation between the test groups at 20-, 30-, 40-, and 50-minute time points (p<0.005). UV treated TiO₂coated specimens showed fastest blood coagulation followed by TiO₂coated and non-coated specimens. Furthermore, platelets appeared at a higher activation state on coated specimens. Gel electrophoresis revealed no difference in protein adsorption among the experimental groups. In summary, TiO₂coatings promoted blood coagulation, and it was further enhanced by UV treatment, which has the potential to hasten the wound healing process in vivo.

The soft tissue-implant interface requires the formation of epithelium and connective tissue seal to hinder microbial infiltration and prevent epithelial down growth. Nanoporous titanium dioxide (TiO₂) surface coatings have shown good potential for promoting soft tissue attachment to implant surfaces. However, the impact of their surface properties on the biological response of gingival cells needs further investigation. This systematic review aimed to investigate the cellular behavior of gingival cells on TiO₂-implant abutment coatings based on in vitro studies. The review was performed to answer the question: “How does the surface characteristic of TiO₂ coatings influence the gingival cell response in in vitro studies?”. A search in MEDLINE/PubMed and the web of science databases from 1990 to 2022 was performed using keywords. A quality assessment of the studies selected was performed using the SciRAP method. A total of 11 publications were selected from the 289 studies that fulfilled the inclusion criteria. The mean reporting and methodologic quality SciRAP scores were 82.7 ± 6.4/100 and 87 ± 4.2/100, respectively. Within the limitations of this in vitro systematic review, it can be concluded that the TiO₂ coatings with smooth nano-structured surface topography and good wettability improve gingival cell response compared to non-coated surfaces.