This study was designed to investigate the effect of nanostructured TiO₂coatings on human gingival fibroblast and to explore the influence of ultraviolet (UV) light on surface wettability and cellular response. Ti‐6Al‐4V titanium alloy discs (n = 96) were divided into three groups: a sol–gel‐derived MetAlive™ (MA) coating; hydrothermal (HT) coating; and a non‐coated (NC) group. Forty‐eight titanium substrates were further treated with UV light for 15 min. The water contact angles of the substrates were measured using the sessile drop method. Human gingival fibroblasts were used to evaluate the cell adhesion strength and cell proliferation on experimental surfaces. The strength of cell adhesion against enzymatic detachment was studied after 6 hr of adhesion using gentle trypsinization for 15 min at room temperature. A fluorescence microscope was used for cell imaging (Zeiss‐stereo‐lumar‐v12), and images were analyzed for cell counting, and the percentage of detached cells were calculated. The proliferation of cultured cells up to 10 days was determined according to the cell activity using Alamar Blue™assay. The HT group had the lowest contact angle value (31.1°) followed by MetAlive™ (35.3°), whereas the NC group had the highest contact angle (50.3°). After UV light treatment, all surfaces become considerably more hydrophilic. There was a significant difference in the amount of adherent cells between sol–gel and HT groups when compared with the NC group (p < .05) with detachment percentages of 35.8%, 36.4%, and 70.7%, respectively. All substrate types showed an increase in cell proliferation rate until 10 days. It can be concluded that nanostructured titanium oxide implant surfaces, obtained by sol–gel and HT coating methods, enhance the surface wettability and improve human gingival fibroblast function in terms of adhesion and proliferation rate when compared with non‐coated surfaces. UV light treatment clearly enhances the wettability of all titanium surfaces.

The soft tissue-implant interface requires the formation of epithelium and connective tissue seal to hinder microbial infiltration and prevent epithelial down growth. Nanoporous titanium dioxide (TiO₂) surface coatings have shown good potential for promoting soft tissue attachment to implant surfaces. However, the impact of their surface properties on the biological response of gingival cells needs further investigation. This systematic review aimed to investigate the cellular behavior of gingival cells on TiO₂-implant abutment coatings based on in vitro studies. The review was performed to answer the question: “How does the surface characteristic of TiO₂ coatings influence the gingival cell response in in vitro studies?”. A search in MEDLINE/PubMed and the web of science databases from 1990 to 2022 was performed using keywords. A quality assessment of the studies selected was performed using the SciRAP method. A total of 11 publications were selected from the 289 studies that fulfilled the inclusion criteria. The mean reporting and methodologic quality SciRAP scores were 82.7 ± 6.4/100 and 87 ± 4.2/100, respectively. Within the limitations of this in vitro systematic review, it can be concluded that the TiO₂ coatings with smooth nano-structured surface topography and good wettability improve gingival cell response compared to non-coated surfaces.

Bioactive glasses (BAG) are surface-active ceramic materials that can be used in bone regeneration due to their known osteoconductive and osteoinductive properties. This systematic review aimed to study the clinical and radiographic outcomes of using BAGs in periodontal regeneration. The selected studies were collected from PubMed and Web of Science databases and included clinical studies investigating the use of BAGs on periodontal bone defect augmentation between January 2000 and February 2022. The identified studies were screened using Preferred Reporting Items for Systematic Reviews and Meta-Analysis (PRISMA) guidelines. A total of 115 full-length peer-reviewed articles were identified. After excluding duplicate articles between the databases and applying the inclusion and exclusion criteria, 14 studies were selected. The Cochrane risk of bias tool for randomized trials was used to assess the selected studies. Five studies compared using BAG with open flap debridement (OFD) without grafting materials. Two of the selected studies were performed to compare the use of BAG with protein-rich-fibrin, one of which also included an additional OFD group. Also, one study evaluated BAG with biphasic calcium phosphate and used a third OFD group. The remaining six studies compared BAG filler with hydroxyapatite, demineralized freeze-dried bone allograft, autogenous cortical bone graft, calcium sulphate -hemihydrate, enamel matrix derivatives, and guided tissue regeneration. This systematic review showed that using BAG to treat periodontal bone defects has beneficial effects on periodontal tissue regeneration.

Establishing a proper soft tissue adhesion around the implant abutment is essential to prevent microbial invasion, inhibit epithelial downgrowth, and obtain an optimal healing process. This systematic review aims to evaluate the real potential of TiO₂ coating on the behavior of peri‐implant soft tissue health and maintenance. A specific aim was to evaluate clinically and histologically the effect of TiO₂ abutment coating on epithelial and connective tissue attachment. Electronic database searches were conducted from 1990 to 2023 in MEDLINE/PubMed and the Web of Science databases. In total, 15 out of 485 publications were included. Eight studies involved humans, and seven were animal studies. Exposure time ranges from 2 days to 5 years. The peri‐implant soft tissue evaluations included clinical assessment (plaque index (PI), peri‐implant probing pocket depth (PPD), and bleeding on probing (BoP)), histological as well as histomorphometric analysis. The Office of Health Assessment and Translation (OHAT) Risk of Bias Rating Tool for Human and Animal Studies was used to evaluate the overall quality of the studies included in the review. The results showed some variation but remained within acceptable limits. Within the limitations of this systematic review, the present findings suggest that TiO₂ coatings seem to influence soft tissue healing. TiO₂‐coated abutments with a roughness value between 0.2 and 0.5 μm enhance soft tissue health. Sol‐gel‐derived TiO₂ coatings induced better soft tissue attachment than noncoated machined abutment surfaces. The anodized titanium abutments demonstrate comparable clinical and histological outcomes to conventional machined abutments. However, there was variation among the included studies concerning TiO₂ coating characteristics and the measured outcomes used to evaluate the soft tissue response, and therefore, quantitative analysis was not feasible. Long‐term in vivo studies with standardized soft tissue analysis and coating surface parameters are necessary before a definitive conclusion can be drawn. OSF Registration No.: 10.17605/OSF.IO/E5RQV.

In vitro studies of implant-tissue attachment are primarily based on two-dimensional cell culture models, which fail to replicate the three-dimensional native human oral mucosal tissue completely. Thus, the present study aimed to describe a novel tissue culture model using pig mandibular block including alveolar bone and gingival soft tissues to evaluate the tissue attachment to titanium implant provided with hydrothermally induced TiO₂ coating. Tissue attachment on TiO₂ coated and non-coated implants were compared. Ti-6Al-4V alloy posts were used to function as implants that were inserted in five pig mandibles. Implants were delivered with two different surface treatments, non-coated (NC) titanium and hydrothermal induced TiO₂ coated surfaces (HT). The tissue-implant specimens were cultured at an air/liquid interface for 7 and 14 days. The tissue-implant interface was analyzed by histological and immunohistochemical stainings. The microscopic evaluation suggests that pig tissue explants established soft and hard tissue attachment to both implant surfaces. The epithelial cells appeared to attach to the coated implant. The epithelium adjacent to the implant abutment starts to change its phenotype during the early days of the healing process. New bone formation was seen within small pieces of bone in close contact with the coated implant. In conclusion, this in vitro model maintains the viability of pig tissue and allows histologically and immunohistochemically evaluate the tissue-implant interface. HT-induced TiO₂ coating seems to have a favorable tissue response. Moreover, this organotypic tissue culture model is applicable for further studies with quantitative parameters to evaluate adhesion molecules present at the implant-tissue interface.