This study reveals the efficiency of the electron beam processing of titanium technogenic material with a high level of impurities and the quality of the obtained metal in correlation to process parameters which are discussed. The influence of the beam power and melting time on the composition variation, morphologies, hardness of metal samples and mass losses is investigated. Based on the different technological parameters, the removal efficiency of impurities is also discussed, and the corresponding experiments are carried out in order to make a comparison. Different thermal process conditions are realized during the single-melt operation. Chemical and metallographic analyses are performed, and the results are discussed. The hardness of the titanium decreases by prolonging the time of the electron beam processing. A maximal overall removal efficiency of 99.975% is seen at 5.5 kW beam power for a 40 min melting time and the best purification of Ti (99.996%) is achieved.

Investigations are carried out and obtained experimental and theoretical data for tantalum scrap recycling by electron beam melting (EBM) is presented in this paper. Different thermal treatment process conditions are realized and results are discussed. A chemical analysis is performed and refining mechanisms for electron beam (EB) refining of Ta are discussed. For the performed experiments the best purification of Ta (99.96) is obtained at 21.6 kW beam power for a melting time of 3 min. A statistical approach is applied for estimation of the material losses and the liquid pool characteristics based on experimentally-obtained data. The aim is to improve the EBM and choosing optimal process conditions, depending on the concrete characteristic requirements. Model-based quality optimization of electron beam melting and refining (EBMR) processes of Ta is considered related to the optimization of the molten pool parameters, connected to the occurring refining processes, and to minimal material losses. Optimization of the process of EBM of Ta is based on overall criteria, giving compromised solutions, depending on the requirements concerning the quality of the performed products. The accumulated data, the obtained results, and the optimization statistical approach allow us to formulate requirements on the process parameters.

In the current work, the possibility of the recycling of technogenic CoCrMo material by electron beam melting is investigated. The influence of thermodynamic and kinetic parameters (temperature and melting time) on the behavior of the main components of the alloy (Co, Cr, and Mo) and other elements (Fe, Mn, Si, W, and Nb) present in it, and on the microstructure of the ingots obtained after e-beam processing is studied. The vapor pressure of the alloy is determined taking into account the activities of the main alloy components (Co, Cr, and Mo). The relative volatility of the metal elements present in the alloy was also evaluated. An assessment of the influence of the temperature and the retention time on the degree of elements removal from CoCrMo technogenic material was made. The results obtained show that the highest degree of refining is achieved at 1860 K and a residence time of 20 min. The conducted EDS analysis of the more characteristic phases observed on the SEM images of the samples shows distinct micro-segregation in the matrix composition.

The hardness of heat (thermally) treated CoCrMo ingots, recycled by electron beam melting and refining (EBMR) of a technogenic CoCrMo material (waste from the dental technology) under different process conditions (temperature and residence time) is examined. The heat treatment consists of two-step heating up to temperatures of 423 K and 1343 K and retention times of 40 and 60 min, respectively. The influence of various loads (0.98 N, 1.96 N, 2.94 N, 4.9 N, and 9.8 N) on the hardness of the CoCrMo alloy, recycled by EBMR, before and after heat treatment is studied. It has been found that regardless of the EBMR process conditions, the obtained samples after heat treatment have similar hardness values (between 494.2 HV and 505.9 HV) and they are significantly lower than the hardness of the specimens before the heat treatment. The highest hardness (600 HV) is measured in the alloy recycled at 1845 K refining temperature for 20 min. This is due to the smaller crystal structure of the resulting alloy and the higher cobalt content. The results obtained show that the heat treatment leads to considerable changes in the microstructure of the CoCrMo ingots recycled by EBMR. With the increase of the e-beam refining temperature, after the heat treatment, the grains’ size increases and the grains’ shape indicates an incomplete phase transition from γ-fcc to ε-hcp phase. This leads to a slight increase in the hardness of the alloy.

The possibility of removing metallic (such as Zr, Fe, Cr, and Zn) impurities and non-metallic (such as [O] and C) impurities from technogenic hafnium through single and double refining in the conditions of electron beam melting (EBM) has been studied. The influence of thermodynamic and kinetic parameters on the degree of removal of these impurities from the base metal under vacuum conditions and within a temperature interval of 2500 K to 3100 K is defined. The relative volatility of metal impurities and the stability of the oxides and carbides present in the base metal are evaluated. The possibility for complete removal of Fe, Cr, Zn, [O], and C during EBM is shown. In the case of double refining, at a temperature of 2700 K for 20 min, the maximum degree of removal of Zr is 46.8%, the achieved highest hafnium purity is 99.004%, and the overall effectiveness of the refining of hafnium from impurities is 53%. There is a correlation between the degree of removal of Zr and the micro-hardness of the Hf ingots obtained after EBM. The weight losses vary in the ranges of 1.5–5.8% and 1–8% under the studied single and double refining processes, respectively.

The current study presents the electron beam melting (EBM) efficiency of copper technogenic material with high impurity content (Se, Te, Pb, Bi, Sn, As, Sb, Zn, Ni, Ag, etc.) by means of thermodynamic analysis and experimental tests. On the basis of the calculated values of Gibbs free energy and the physical state of the impurity (liquid and gaseous), a thermodynamic assessment of the possible chemical interactions occurring in the Cu-Cu₂O-Me_x system in vacuum in the temperature range 1460–1800 K was made. The impact of the kinetic parameters (temperature and refining time) on the behaviour and the degree of removal of impurities was evaluated. Chemical and metallographic analysis of the obtained ingots is also discussed.