Edible films based on fish-skin gelatin incorporated with chitosan and/or clove essential oil were elaborated and their antimicrobial activity was tested on Lactobacillus acidophilus, Pseudomonas fluorescens, Listeria innocua, and Escherichia coli. The films incorporated with the clove essential oil were the most effective although differences were observed depending on the biopolymeric matrix in which it was included. When a clove added film was applied to the preservation of raw sliced salmon, a reduction of the growth of total bacteria was observed after 11 days of storage at 2°C. So, edible films based on fish gelatin can be used as an active packaging applied to fish products.

This study aims to determine the potential antioxidant, antihypertensive, hypoglycaemic and nootropic activity of a purified polyphenolic extract from the halophyte ice plant (Mesembryanthemum crystallinum). The ice plant extract showed good antioxidant activity measured by DPPH, ORAC, TEAC, FRAP and ferrous ion chelating activity. Moreover, the extract showed potent ACE, DPP-IV and PEP-inhibitory activity (90.5%, 98.6% and 73.1%, respectively, at a final concentration of 1 mg/mL). The extract was fractionated and the fraction with the highest content of total phenolic compounds showed the highest bioactivity, suggesting that polyphenols could be mainly responsible for the abovementioned activities. The tentative polyphenol identification by HPLC-ESI-QTOF-MS in this fraction revealed that flavones (>65%) are the major group, with apigenin (38%) predominating, followed by diosmin (17.7%) and luteolin (11.9%). They could presumably be the main elements responsible for the enzymatic inhibition activity. Additionally, 4-hydroxybenzoic acid, p-coumaric acid and a hydroxycinnamic acid derivative (2-O-(p-cumaroyl)-l-malic acid) were found in the extract. To our knowledge, this is the first time that some of these activities have been reported for halophyte extracts.

The aim of the present work was to fortify yogurt by adding a stripped weakfish (Cynoscion guatucupa) protein hydrolysate obtained with the enzyme Protamex and microencapsulated by spray drying, using maltodextrin (MD) as wall material. The effects on the physicochemical properties, syneresis, texture, viscoelasticity, antioxidant and ACE inhibitory activities of yogurt after 1 and 7 days of storage were evaluated. In addition, microbiological and sensory analyses were performed. Four yogurt formulations were prepared: control yogurt (without additives, YC), yogurt with MD (2.1%, YMD), with the free hydrolysate (1.4%, YH) and the microencapsulated hydrolysate (3.5%, YHEn). Yogurts to which free and microencapsulated hydrolysates were added presented similar characteristics, such as a slight reduction in pH and increased acidity, with a greater tendency to present a yellow color compared with the control yogurt. Moreover, they showed less syneresis, the lowest value being that of YHEn, which also showed a slight increase in cohesiveness and greater rheological stability after one week of storage. All yogurts showed high counts of the microorganisms used as starters. The hydrolysate presence in both forms resulted in yogurts with antioxidant activity and potent ACE-inhibitory activity, which were maintained after 7 days of storage. The incorporation of the hydrolysate in the microencapsulated form presented greater advantages than the direct incorporation, since encapsulation masked the fishy flavor of the hydrolysate, resulting in stable and sensorily acceptable yogurts with antioxidant and ACE inhibitory activities.

Ancestral Andean crop flours (ACF) from Ecuador such as camote (Ipomea Batatas), oca (Oxalis tuberosa), achira (Canna indica), mashua (Tropaeolum tuberosum), white arracacha (Arracacia xanthorrhiza), taro (Colocasia esculenta) and tarwi (Lupinus mutabilis sweet) were characterized in terms of physico-chemical and techno-functional properties in order to identify their potential as new alternative ingredients in food products. Flour from camote, oca, achira and arracacha showed a low protein content ( G″, this being very similar in camote, achira and tarwi flours. The exception was taro with G′ < G″. Mashua flour registered the highest value for phenol content (60.8 µg gallic acid equivalents/g of sample); the content of phenols was not exclusively responsible for the antioxidant activity, since flours with the highest activity were arracacha and tarwi, which presented the lowest phenol content among all flours. Principal component analyses (PCA) showed a high correlation between moisture, fiber, solubility and water absorption capacity, with viscoelastic behavior and total phenolic content; while starch content was correlated with melting temperature, poorly and inversely related to protein and fat. For PC1, achira, camote and taro flours were very similar, and different from oca and mashua flours. Tarwi showed its own characteristics according to PC1 and 2. Because of their properties, Andean crop flours could have a great potential for use in food technology.

In this study, edible packaging based on discarded green banana (Musa acuminata AAA) flour (whole banana and banana peel flours) was developed for food applications. Films were characterized in terms of film-forming ability, mechanical, barrier, thermal, microbiological, and sensory properties. The film forming solutions were studied for rheological properties. Two formulations were selected based on their film-forming ability: whole banana flour (2.5%), peel flour (1.5%) and glycerol (1.0 %, F-1.0 G or 1.5%, F-1.5 G). Adding 1.5% plasticizer, due to the hygroscopic effect, favored the water retention of the films, increasing the density, which also resulted in a decrease in lightness and transparency. Water activity shows no difference between the two formulations, which were water resistant for at least 25 h. DSC results showed a similar melting temperature (Tm) for both films, around 122 °C. Both films solutions showed a viscoelastic behavior in the frequency spectrum, being the elastic modulus greater in F-1.0 G film than F-1.5 G film at low frequency. F-1.0 G film was less firm, deformable and elastic, with a less compact structure and a rougher surface as confirmed by AFM, favoring a higher water vapor permeability with respect to F.1.5 G film. Microorganisms such as Enterobacteria and Staphylococcus aureus were not found in the films after a period of storage (1 year under ambient conditions). The F-1.0 G film with added spices (cumin, oregano, garlic, onion, pepper, and nutmeg) was tested for some food applications: as a snack (with or without heat treatment) and as a wrap for grilled chicken. The performance of the seasoned film during chilled storage of chicken breast was also studied. Sensory evaluation showed good overall acceptability of all applications. In addition, the chicken breast wrapped with the seasoned film registered lower counts (1-log cycle) than the control (covered with a polystyrene bag) and the film without spices. Green banana flour is a promising material to develop edible films for food applications.