Thermo-electrochemical cells (also known as thermocells, TECs) represent a promising technology for harvesting and exploiting low-grade waste heat (<100–150 °C) ubiquitous in the modern environment. Based on temperature-dependent redox reactions and ion diffusion, emerging liquid-state thermocells convert waste heat energy into electrical energy, generating power at low costs, with minimal material consumption and negligible carbon footprint. Recent developments in thermocell performances are reviewed in this article with specific focus on new redox couples, electrolyte optimisation towards enhancing power output and operating temperature regime and the use of carbon and other nanomaterials for producing electrodes with high surface area for increasing current density and device performance. The highest values of output power and cell potentials have been achieved for the redox ferri/ferrocyanide system and Co^2+/3+, with great opportunities for further development in both aqueous and non-aqueous solvents. New thermoelectric applications in the field include wearable and portable electronic devices in the health and performance-monitoring sectors; using body heat as a continuous energy source, thermoelectrics are being employed for long-term, continuous powering of these devices. Energy storage in the form of micro supercapacitors and in lithium ion batteries is another emerging application. Current thermocells still face challenges of low power density, conversion efficiency and stability issues. For waste-heat conversion (WHC) to partially replace fossil fuels as an alternative energy source, power generation needs to be commercially viable and cost-effective. Achieving greater power density and operations at higher temperatures will require extensive research and significant developments in the field.

In this study, we report the effect of intercalation of dimethyl sulfoxide (DMSO) and urea molecules into the interlayer space of Ti₃C₂T_x MXene on the dielectric properties of poly(vinylidene fluoride) (PVDF)/MXene polymer nanocomposites. MXenes were obtained by a simple hydrothermal method using Ti₃AlC₂ and a mixture of HCl and KF, and they were then intercalated with DMSO and urea molecules to improve the exfoliation of the layers. Then, nanocomposites based on a PVDF matrix loading of 5–30 wt.% MXene were fabricated by hot pressing. The powders and nanocomposites obtained were characterized by using XRD, FTIR, and SEM. The dielectric properties of the nanocomposites were studied by impedance spectroscopy in the frequency range of 10²–10⁶ Hz. As a result, the intercalation of MXene with urea molecules made it possible to increase the permittivity from 22 to 27 and to slightly decrease the dielectric loss tangent at a filler loading of 25 wt.% and a frequency of 1 kHz. The intercalation of MXene with DMSO molecules made it possible to achieve an increase in the permittivity up to 30 at a MXene loading of 25 wt.%, but the dielectric loss tangent was increased to 0.11. A discussion of the possible mechanisms of MXene intercalation influence on the dielectric properties of PVDF/Ti₃C₂T_x MXene nanocomposites is presented.

The development of new electrode materials for electrochemical systems for various purposes is a significant and in-demand task of scientific research. Layered transition metal carbides and nitrides, known as MXenes, show great potential for use as electrodes in electrochemical energy storage devices operating in aqueous electrolytes. In this work, a multilayer Ti₃C₂T_x MXene was obtained from a Ti₃AlC₂ precursor and studied as the electrode material of a symmetrical supercapacitor with an aqueous LiCl electrolyte. The formation of the MXene structure was confirmed by the data from X-ray phase analysis and scanning electron microscopy. The X-ray diffraction pattern showed the disappearance of the main reflections related to the Ti₃AlC₂ phase and the shift of the reflection peak (002) from 9.4° to 6.7°, which indicated successful etching of the Al layers from the Ti₃AlC₂ precursor. At electrolyte concentrations of 1, 5, 10, and 20 M, the supercapacitors demonstrated high specific capacitances of 105, 120, 126, and 151 F·g⁻¹ at a scan rate of 5 mV·s⁻¹. In addition, an increase in the LiCl concentration contributed to the expansion of the potential window from 0.7 to 1 V. It was shown that the contribution of the surface capacitance to the total capacitance of the electrode is about 40% and depends little on the scan rate. In addition, the symmetrical supercapacitor with 5 M electrolyte showed good cyclic stability with capacitance retention of 88% over 10,000 cycles. The parameters of the main components of the physical processes of supercapacitors based on Ti₃C₂T_x were determined by the method of impedance spectroscopy.