In this work we demonstrate comprehensive studies on graphene oxide (GO) and reduced graphene oxide (rGO) based saturable absorbers (SA) for mode-locking of Er-doped fiber lasers. The paper describes the fabrication process of both saturable absorbers and detailed comparison of their parameters. Our results show, that there is no significant difference in the laser performance between the investigated SA. Both provided stable, mode-locked operation with sub-400 fs soliton pulses and more than 9 nm optical bandwidth at 1560 nm center wavelength. It has been shown that GO might be successfully used as an efficient SA without the need of its reduction to rGO. Taking into account simpler manufacturing technology and the possibility of mass production, GO seems to be a good candidate as a cost-effective material for saturable absorbers for Er-doped fiber lasers.

Transition metal dichalcogenides (TMDCs) are attractive for variety of nanoscale electronics and optoelectronics devices due to their unique properties. Despite growing progress in the research field of TMDCs, many of their properties are still unknown. In this letter, we report measurements of Raman spectra of rhenium diselenide (ReSe₂) and tin diselenide (SnSe₂) layered semiconductor nanosheets as a function of temperature (70–400 K). We analyze the temperature dependence of the positions of eight ReSe₂ modes and SnSe₂ A_1g mode. All observed Raman mode shifts exhibit nonlinear temperature dependence at low temperatures which is explained by optical phonon decay process into two or three acoustics phonons. The first order temperature coefficients (χ), determined for high temperatures, of rhenium diselenide Raman modes are in the range between −0.0033 and −0.0118 cm⁻¹/K, whereas χ of tin diselenide A_1g mode was −0.0129 cm⁻¹/K. Our findings are useful for further analysis of phonon and thermal properties of these dichalcogenide layered semiconductors.

We present a novel approach for the simultaneous determination of the thermal conductivity κ and the total interface conductance g of supported 2D materials by the enhanced opto-thermal method. We harness the property of the Gaussian laser beam that acts as a heat source, whose size can easily and precisely be controlled. The experimental data for multi-layer graphene and MoS₂ flakes are supplemented using numerical simulations of the heat distribution in the Si/SiO2/2D material system. The procedure of κ and g extraction is tested in a statistical approach, demonstrating the high accuracy and repeatability of our method.