In this work we demonstrate comprehensive studies on graphene oxide (GO) and reduced graphene oxide (rGO) based saturable absorbers (SA) for mode-locking of Er-doped fiber lasers. The paper describes the fabrication process of both saturable absorbers and detailed comparison of their parameters. Our results show, that there is no significant difference in the laser performance between the investigated SA. Both provided stable, mode-locked operation with sub-400 fs soliton pulses and more than 9 nm optical bandwidth at 1560 nm center wavelength. It has been shown that GO might be successfully used as an efficient SA without the need of its reduction to rGO. Taking into account simpler manufacturing technology and the possibility of mass production, GO seems to be a good candidate as a cost-effective material for saturable absorbers for Er-doped fiber lasers.

We report, for the first time to our knowledge, the usage of black phosphorus (BP) as a saturable absorber for the mode locking of a thulium-doped fiber laser. We have experimentally shown that BP exhibits saturable absorption in the 2 μm wavelength range and supports ultrashort pulse generation. The saturable absorber was based on mechanically exfoliated BP deposited on a fiber connector tip. The laser was capable of generating 739 fs pulses centered at 1910 nm. Our results show that BP might be considered as a universal broadband saturable absorber that could successfully compete with graphene or other low-dimension nanomaterials.

Low-dimensional materials, due to their unique and versatile properties, are very interesting for numerous applications in electronics and optoelectronics. Recently rediscovered black phosphorus, with a graphite-like layered structure, can be effectively exfoliated up to the single atomic layer called phosphorene. Contrary to graphene, it possesses a direct band gap controllable by the number of stacked atomic layers. For those reasons, black phosphorus is now intensively investigated and can complement or replace graphene in various photonics and electronics applications. Here, we demonstrate that black phosphorus can serve as a broadband saturable absorber and can be used for ultrashort optical pulse generation. The mechanically exfoliated ∼300 nm thick layers of black phosphorus were transferred onto the fiber core, and under pulsed excitation at 1560 nm wavelength, its transmission increases by 4.6%. We have demonstrated that the saturable absorption of black phosphorus is polarization sensitive. The fabricated device was used to mode-lock an Er-doped fiber laser. The generated optical solitons with the 10.2 nm bandwidth and 272 fs duration were centered at 1550 nm. The obtained results unambiguously show that black phosphorus can be effectively used for ultrashort pulse generation with performances similar or even better than currently used graphene or carbon nanotubes. This application of black phosphorus proves its great potential to future practical use in photonics.

Optics InfoBase is the Optical Society's online library for flagship journals, partnered and copublished journals, and recent proceedings from OSA conferences.

In this Letter, we demonstrate a mode-locked Er-doped fiber laser incorporating antimony telluride (Sb₂Te₃) topological insulator (TI) as a saturable absorber (SA). The laser was capable of generating 270 fs-short soliton pulses at 1560 nm wavelength, which are the shortest solitons generated with a TI-based saturable absorber so far. In order to form a saturable absorber, a bulk piece of Sb₂Te₃ was deposited on a side-polished single-mode fiber with the presence of a low refractive index polymer. Such saturable absorber exhibits modulation depth at the level of 6% with less than 3 dB of non-saturable losses. Our study shows that TI-based saturable absorbers with evanescent field interaction might compete with SAs based on carbon nanomaterials, like graphene or nanotubes. Additionally, thanks to the interaction with the evanescent field, the material is not exposed to high optical power, which allows to avoid optical or thermal damage.

In this work we present for the first time, to the best of our knowledge, a stretched-pulse mode-locked fiber laser based on topological insulator. As a saturable absorber (SA) a ~0.5 mm thick lump of antimony telluride (Sb₂Te₃) deposited on a side-polished fiber was used. Such a SA introduced 6% modulation depth with 43% of non-saturable losses, which is sufficient for supporting stretched-pulse mode-locking. The ring laser resonator based on Er-doped active fiber with managed intracavity dispersion was capable of generating ultrashort optical pulses with full width at half maximum (FWHM) of 30 nm centered at 1565 nm. The pulses with duration of 128 fs were repeated with a frequency of 22.32 MHz.