To reveal the influence mechanism of ettringite (AFt) crystals and microstructure characteristics on the strength of calcium-based stabilized soil, the strengths and microscopic properties of seven groups of stabilized soil samples were studied systematically through unconfined compressive strength, scanning electron microscope (SEM), X-ray diffraction (XRD), thermogravimetry (TG), and Fourier transform infrared spectroscopy (FTIR) testing methods. The results indicate that the strength of the cement-stabilized soil is relatively high because abundant calcium silicate hydrate (CSH) gels coat the outer surface of soil particles to cement together. For the cement–gypsum-stabilized soil, superabundant thick and long AFt crystals make the pores in soil particles larger, and the sample becomes looser, resulting in lower strength than that of the cement-stabilized soil. However, the strength of the cement–gypsum–lime-stabilized soil is slightly stronger than that of the cement-stabilized soil, for the reason that the appropriate amount of fine AFt crystals fill the macropores between soil particles to form a network space structure and sufficient CSH gels cement the soil particles and the AFt crystals network space structure tightly together. It could be suggested that the components of calcium-based stabilizer should consider the optimal production balance between CSH gels and fine AFt crystals.

To elucidate the relationship between compressive strength and pore structure of the high water grouting material with different water-binder ratios and CaO contents, the compressive strength was tested while pore structure including pore characteristic parameters and pore diameter distribution were investigated by BET, MIP, and 3D-XRM. Moreover, the evolution of hydration products was observed by TGA and SEM, illustrating the reactive mechanism of the material. Furthermore, the grey correlation coefficients between compressive strength and pore structure parameters were illustrated according to the grey correlation theory. The results show that CaO content in lime is proportional to the compressive strength with the water-binder ratio of 1.0 or 1.5, while the inverse trend appears with the water-binder ratio of 2.0. The high water grouting material belongs to the macropore material with the pores mainly within 100 nm to 2 μm. Its hydration products contain ettringite crystals, aluminum gels, and C-S-H gels. The productions of the hydration products are positively correlated with its compressive strength. In addition, the compressive strength of the high water grouting material is closely related to the pore characteristic parameters and the pore size distribution, especially the porosity, the most probable pore diameter, and the pore volumes within 100~500 nm and 10~100 nm.

In the present paper, the monotonic axial compression test of gangue aggregate concrete filled Fiber reinforced polymer (FRP) and thin-walled steel double tubular columns (DTCC) was carried out, and the gangue aggregate concrete filled FRP tubular columns (CFFT) were designed as a comparison. The main experimental factors were the confinement level of the FRP jacket, the relative diameter ratio (the ratio of the outer diameter of the steel tube to the inner diameter of the FRP jacket), and the different strengths of gangue aggregate concrete. The test results show that the bearing capacity and ductility of gangue aggregate concrete in CFFT were significantly improved. As the local buckling of thin-walled steel tube was effectively inhibited, the load bearing capacity of DTCC was further improved compared with CFFT, but the change of dilation behavior and ductility was insignificant. By analyzing the bi-directional stress state of the steel tube, the confinement level of the external FRP jacket was the most sensitive factor affecting the hoop stress of the steel tube, and the axial stress was obviously weakened under the bi-directional stress state. In addition, with the increase of steel tube diameter, the confinement effect of steel tube in DTCC became more obvious.