To reveal the influence mechanism of ettringite (AFt) crystals and microstructure characteristics on the strength of calcium-based stabilized soil, the strengths and microscopic properties of seven groups of stabilized soil samples were studied systematically through unconfined compressive strength, scanning electron microscope (SEM), X-ray diffraction (XRD), thermogravimetry (TG), and Fourier transform infrared spectroscopy (FTIR) testing methods. The results indicate that the strength of the cement-stabilized soil is relatively high because abundant calcium silicate hydrate (CSH) gels coat the outer surface of soil particles to cement together. For the cement–gypsum-stabilized soil, superabundant thick and long AFt crystals make the pores in soil particles larger, and the sample becomes looser, resulting in lower strength than that of the cement-stabilized soil. However, the strength of the cement–gypsum–lime-stabilized soil is slightly stronger than that of the cement-stabilized soil, for the reason that the appropriate amount of fine AFt crystals fill the macropores between soil particles to form a network space structure and sufficient CSH gels cement the soil particles and the AFt crystals network space structure tightly together. It could be suggested that the components of calcium-based stabilizer should consider the optimal production balance between CSH gels and fine AFt crystals.

This work aimed to investigate the effects of steel tube corrosion on the axial ultimate load-bearing capacity (AULC) of circular thin-walled concrete-filled steel tubular (CFST) members. Circular thin-walled CFST stub column specimens were made of steel tubes with various wall-thicknesses. These CFST column specimens were subjected to an accelerated corrosion test, where the steel tubes were corroded to different degrees of corrosion. Then, these CFST specimens with corroded steel tubes experienced an axial static loading test. Results show that the failure patterns of circular thin-walled CFST stub columns with corroded steel tubes are different from those of the counterpart CFST columns with ordinary wall-thickness steel tubes, which is a typical failure mode of shear bulging with slight local outward buckling. The ultimate strength and plastic deformation capacity of the CFST specimens decreased with the increasing degree of steel corrosion. The failure modes of the specimens still belonged to ductile failure because of the confinement of outer steel tube. The degree of steel tube corrosion, diameter-to-thickness ratio, and confinement coefficient had substantial influences on the AULC and the ultimate compressive strength of circular thin-walled CFST stub columns. A simple AULC prediction model for corroded circular thin-walled CFST stub columns was presented through the regression of the experimental data and parameter analysis.

Modular steel buildings offer the advantages of time-saving construction, reduced on-site work, and less resource waste. The mechanical behavior of modular connections is complex, depending on the type of connecting method and the load-transferring path. The aim of this paper is to offer an overview of the methods for creating inter-module connections. First, we discuss the existing inter-module connections, including vertical connections, horizontal connections, and module-to-concrete-core-wall connections. Then, the mechanical performance and simplified models of the inter-module connections are reviewed in detail; these have a significant influence on the development of modular steel buildings. Finally, the prospects of module-to-module connection are summarized. Despite the increasing amount of research that explores module-to-module connections, fully modular buildings have not yet been achieved, hindering the further development and use of modular steel buildings. In this context, self-locking connections and laminated double-beam connections are proposed, with the aim of promoting the increased use of modular steel buildings.

To investigate the residual bending strength of a corroded H-shaped steel beam in an underground coal mining environment, the law governing the degradation of the mechanical properties of corroded steel was first investigated through tensile testing. Subsequently, a four-point bending test was conducted on corroded H-shaped steel beams. The influence of the corrosion rate and sustained loading ratio on the residual bending performance of a corroded H-beam was investigated. The results reveal that the uniform corrosion and uneven corrosion of the steel occurred simultaneously. Additionally, pits with a small size appeared on the steel surface and the number of these pits increased with the corrosion time. Four different fracture modes were observed after the tensile test, and the yield strength and ultimate strength of the corroded steel decreased as the corrosion rate increased. In the bending test, the failure mode of the corroded H-shaped steel beam was not changed by the corrosion. The bearing capacity, stiffness, and ductility of the corroded H-shaped steel beams decreased with the increase in the corrosion rate, and the sustained loading further decreased the bearing capacity. Finally, a simple method for assessing the yield load and ultimate load of corroded H-shaped steel beams is proposed.

In the present paper, the monotonic axial compression test of gangue aggregate concrete filled Fiber reinforced polymer (FRP) and thin-walled steel double tubular columns (DTCC) was carried out, and the gangue aggregate concrete filled FRP tubular columns (CFFT) were designed as a comparison. The main experimental factors were the confinement level of the FRP jacket, the relative diameter ratio (the ratio of the outer diameter of the steel tube to the inner diameter of the FRP jacket), and the different strengths of gangue aggregate concrete. The test results show that the bearing capacity and ductility of gangue aggregate concrete in CFFT were significantly improved. As the local buckling of thin-walled steel tube was effectively inhibited, the load bearing capacity of DTCC was further improved compared with CFFT, but the change of dilation behavior and ductility was insignificant. By analyzing the bi-directional stress state of the steel tube, the confinement level of the external FRP jacket was the most sensitive factor affecting the hoop stress of the steel tube, and the axial stress was obviously weakened under the bi-directional stress state. In addition, with the increase of steel tube diameter, the confinement effect of steel tube in DTCC became more obvious.