A multilevel factorial design of 2³ with 12 experiments was developed for the preparation of cellulose nanocrystals (CNC) from Agave tequilana Weber var. Azul bagasse, an agro-industrial waste from tequila production. The studied parameters were acid type (H₂SO₄ and HCl), acid concentration (60 and 65 wt% for H₂SO₄, 2 and 8N for HCl) temperature (40 and 60 °C for H₂SO₄, 50 and 90 °C for HCl), and hydrolysis time (40, 55 and 70 min for H₂SO₄; and 30, 115 and 200 min for HCl). The obtained CNC were physical and chemically characterized using dynamic light scattering (DLS), atomic force microscopy (AFM), Fourier-transform infrared spectroscopy (FT-IR), X-ray photoelectron spectroscopy (XPS), and X-ray diffraction (XDR) techniques. The maximum CNC yield was 90 and 96% for HCL and H₂SO₄, respectively, and the crystallinity values ranged from 88–91%. The size and morphology of A. tequilana CNC strongly depends on the acid type and hydrolysis time. The shortest CNC obtained with H₂SO₄ (65 wt%, 40 °C, and 70 min) had a length of 137 ± 68 nm, width 33 ± 7 nm, and height 9.1 nm, whereas the shortest CNC obtained with HCl (2 N, 50 °C and 30 min) had a length of 216 ± 73 nm, width 69 ± 17 nm, and height 8.9 nm. In general, the obtained CNC had an ellipsoidal shape, whereas CNC prepared from H₂SO₄ were shorter and thinner than those obtained with HCl. The total sulfate group content of CNC obtained with H₂SO₄ increased with time, temperature, and acid concentration, exhibiting an exponential behavior of $C_{SG}=a{e}^{bt}$.

In this work, cellulose nanocrystals (CNCs), bleached cellulose nanofibers (bCNFs), and unbleached cellulose nanofibers (ubCNFs) isolated by acid hydrolysis from Agave tequilana Weber var. Azul bagasse, an agro-waste from the tequila industry, were used as reinforcements in a thermoplastic starch matrix to obtain environmentally friendly materials that can substitute contaminant polymers. A robust characterization of starting materials and biocomposites was carried out. Biocomposite mechanical, thermal, and antibacterial properties were evaluated, as well as color, crystallinity, morphology, rugosity, lateral texture, electrical conductivity, chemical identity, solubility, and water vapor permeability. Pulp fibers and nanocelluloses were analyzed via SEM, TEM, and AFM. The water vapor permeability (WVP) decreased by up to 20.69% with the presence of CNCs. The solubility decreases with the presence of CNFs and CNCs. The addition of CNCs and CNFs increased the tensile strength and Young’s modulus and decreased the elongation at break. Biocomposites prepared with ubCNF showed the best tensile mechanical properties due to a better adhesion with the matrix. Images of bCNF-based biocomposites demonstrated that bCNFs are good reinforcing agents as the fibers were dispersed within the starch film and embedded within the matrix. Roughness increased with CNF content and decreased with CNC content. Films with CNCs did not show bacterial growth for Staphylococcus aureus and Escherichia coli. This study offers a new theoretical basis since it demonstrates that different proportions of bleached or unbleached nanofibers and nanocrystals can improve the properties of starch films.

A multilevel factorial design of 23 with 12 experiments was developed for the preparation of cellulose nanocrystals (CNC) from Agave tequilana Weber var. Azul bagasse. The studied parameters were acid type (H2SO4 and HCl), acid concentration (60 and 65 wt% for H2SO4, 2 and 8N for HCl) temperature (40 and 60°C for H2SO4, 50 and 90°C for HCl), and hydrolysis time (40, 55 and 70 min for H2SO4, 30, 115 and 200 min for HCl). The obtained CNC were physical and chemically characterized using dynamic light scattering (DLS), atomic force microscopy (AFM), Fourier-transform infrared spectroscopy (FT-IR), X-ray photoelectron spectroscopy (XPS), and X-ray diffraction (XDR) techniques. The size and morphology of A. tequilana CNC strongly depend on the acid type and hydrolysis parameters. The shortest CNC were obtained with H2SO4 (65 wt%, 40 °C, and 70 min) had a length of 137 ± 68 nm, width 33 ± 7 nm, and height 9.1 nm, whereas the shortest CNC obtained with HCl (2 N, 50 °C and 30 min) had a length of 216 ± 73 nm, width 69 ± 17 nm, and height 8.9 nm. CNC prepared from H2SO4 resulted shorter and thinner than those obtained with HCl. The total sulfate groups content in CNC obtained with H2SO4 increase with time agree to CSG=aebt, and increases with temperature and acid concentration.

Polyethylene terephthalate (PET) waste has become a major challenge for the conservation of the environment due to difficult degradation. For this reason, it is important to develop new recycling strategies for reusing this waste. In this work, the electrospinning technique was used to synthesize composite nanofibers of polyvinylpyrrolidone (PVP), recycling PET (RPET) that was obtained from the chemical recycling of postconsumer PET with glycolysis and styrene (ST) as a crosslinking agent. The polymer solutions were analyzed by viscosity and frequency sweeping, while the composite nanofibers were characterized by scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), thermogravimetric analysis/differential scanning calorimetry (TGA/DSC), and nanoindentation to compare their properties. The PVP nanofibers presented an average diameter of 257 nm; the RPET/PVP and RPET/PVP/ST composite nanofibers had average diameters of 361 nm and 394 nm, respectively; and the modulus of elasticity and hardness of the RPET/PVP/ST composite nanofibers were 29 and 20 times larger, respectively, than those of the PVP nanofibers. With the synthesis of these composite nanofibers, a new approach to PET recycling is presented.

New asphalt mixtures have been improved by using fibers (polypropylene, polyester, asbestos, carbon, glass, nylon, lignin, coconut, sisal, recycled rubber, PET, wood, bamboo, and cellulose), reducing the temperature and compaction energy for their collocation, minimizing the impact on the environment, increasing the tenacity and resistance to cracking of hot mix asphalt (HMA), preventing asphalt drainage in a Stone Mastic Asphalt (SMA). Hence, this paper aims to evaluate the influence of the chemical (lignin content, ash, viscosity, degree of polymerization, and elemental analysis), morphological (SEM), spectroscopic (FTIR-ATR and XRD), and calorimetric (ATG and DSC) properties of celluloses from bagasse Agave tequilana Weber var. Azul (ABP), corrugated paperboard (CPB) and commercial cellulose fiber (CC) as Schellenberg drainage (D) inhibitors of the SMA. The ABP was obtained through a chemical process by alkaline cooking, while CPB by a mechanical refining process. The chemical, morphological, spectroscopic, and calorimetric properties were similar among the analyzed celluloses, but CPB and ABP cellulose are excellent alternatives to CC cellulose for inhibiting drainage. However, CPB is the most effective at low concentrations. This is attributed to its morphology, which includes roughness, waviness, filament length, orientation, and diameter, as well as its lignin content and crystallinity.

In this work, cellulose nanocrystals (CNCs) were obtained from the wood of Acacia farnesiana L. Willd (Huizache) via acid hydrolysis; then, they were used to reinforce polyacrylic acid–co-acrylamide (AAc/AAm) hydrogels synthesized in a solution process via in situ free radical photopolymerization. The nanomaterials were characterized using atomic force microscopy, dynamic light scattering (DLS), and the residual charge on the CNCs; the nanohydrogels were characterized using infrared spectroscopy, scanning electron microscopy, swelling kinetics, and Young’s modulus. Soluble-grade cellulose presented 94.6% α-cellulose, 0.5% β-cellulose, and 2.7% γ-cellulose, as well as a viscosity of 8.25 cp and a degree of polymerization (DP) of 706. The CNCs averaged 180 nm in length and 20 nm in width. In the nanohydrogels, it was observed that the swelling kinetic behavior followed the Schott kinetic model, at times lower than 500 h; after that, it became linear. The results show that the hydrogel swelling capacity depended on the crosslinking agent and CNC concentration, as well as the CNC chemical and morphological properties, rather than the CNC source. The hydrogels with CNCs exhibited a decreased swelling degree compared to the hydrogels without CNCs. Young’s modulus increased with CNC presence and depended on the concentration and characteristics of the CNC as a crosslinking agent.