Mango by-products are important sources of bioactive compounds generated by agro-industrial process. During mango processing, 35–60% of the fruit is discarded, in many cases without treatment, generating environmental problems and economic losses. These wastes are constituted by peels and seeds (tegument and kernel). The aim of this review was to describe the extraction, identification, and quantification of bioactive compounds, as well as their potential applications, published in the last ten years. The main bioactive compounds in mango by-products are polyphenols and carotenoids, among others. Polyphenols are known for their high antioxidant and antimicrobial activities. Carotenoids show provitamin A and antioxidant activity. Among the mango by-products, the kernel has been studied more than tegument and peels because of the proportion and composition. The kernel represents 45–85% of the seed. The main bioactive components reported for the kernel are gallic, caffeic, cinnamic, tannic, and chlorogenic acids; methyl and ethyl gallates; mangiferin, rutin, hesperidin, and gallotannins; and penta-O-galloyl-glucoside and rhamnetin-3-[6-2-butenoil-hexoside]. Meanwhile, gallic acid, ferulic acid, and catechin are reported for mango peel. Although most of the reports are at the laboratory level, they include potential applications in the fields of food, active packaging, oil and fat, and pharmaceutics. At the market level, two trends will stimulate the industrial production of bioactive compounds from mango by-products: the increasing demand for industrialized fruit products (that will increase the by-products) and the increase in the consumption of bioactive ingredients.

Chemical and Mechanical Evaluation of Bio-composites Based on Thermoplastic Starch and Wood Particles Prepared by Thermal Compression

The growing demand for cellulosic pulp presents an opportunity to explore alternatives to this material, focusing on utilizing agro-industrial residues. Mango’s tegument is a rich source of cellulose, making it a valuable raw material for manufacturing single-use articles or blends with biopolymers. In this sense, employing conventional alkaline and acid chemical treatments, the mango’s tegument was treated to obtain cellulosic pulp. The teguments were subjected to treatment with alkaline solutions (2% and 4% NaOH w/v) at 80 °C for 1 or 2 h or with an acetic acid solution (1:1 or 1:2 CH₃COOH:H₂O₂) at 60–70 °C for 1 or 2 h. After treatment, an evaluation was conducted to assess the yield, color, chemical analysis, and structural, thermal, and morphological properties. The alkali treatments produced cellulosic pulps with a light color with 37–42% yield and reduced hemicellulose content. The acid treatments produced orange–brown cellulosic pulp with 47–48% yield and higher hemicellulose content. The acid pulps were thermally more stable (maximum decomposition at 348–357 °C) than the alkali pulps (maximum decomposition at 316–321 °C). The crystallinity index demonstrated that both treatments increased the crystallinity of the cellulose pulps compared with the untreated tegument. The thermal stability of cellulosic pulp at the processing temperatures of disposable tableware (50–120 °C) revealed that plates, bowls, trays, and cups could be produced. Another potential application is as a component of blends with biopolymers to make straws or rigid food packaging (trays) with reinforced structures.

In this work, cellulose nanocrystals (CNCs), bleached cellulose nanofibers (bCNFs), and unbleached cellulose nanofibers (ubCNFs) isolated by acid hydrolysis from Agave tequilana Weber var. Azul bagasse, an agro-waste from the tequila industry, were used as reinforcements in a thermoplastic starch matrix to obtain environmentally friendly materials that can substitute contaminant polymers. A robust characterization of starting materials and biocomposites was carried out. Biocomposite mechanical, thermal, and antibacterial properties were evaluated, as well as color, crystallinity, morphology, rugosity, lateral texture, electrical conductivity, chemical identity, solubility, and water vapor permeability. Pulp fibers and nanocelluloses were analyzed via SEM, TEM, and AFM. The water vapor permeability (WVP) decreased by up to 20.69% with the presence of CNCs. The solubility decreases with the presence of CNFs and CNCs. The addition of CNCs and CNFs increased the tensile strength and Young’s modulus and decreased the elongation at break. Biocomposites prepared with ubCNF showed the best tensile mechanical properties due to a better adhesion with the matrix. Images of bCNF-based biocomposites demonstrated that bCNFs are good reinforcing agents as the fibers were dispersed within the starch film and embedded within the matrix. Roughness increased with CNF content and decreased with CNC content. Films with CNCs did not show bacterial growth for Staphylococcus aureus and Escherichia coli. This study offers a new theoretical basis since it demonstrates that different proportions of bleached or unbleached nanofibers and nanocrystals can improve the properties of starch films.