Magnesium (Mg) alloys have demonstrated tremendous potential in biomedical applications, emerging as promising metallic biomaterials due to their biocompatibility, degradability, and favorable mechanical properties. However, their practical implementation faces significant limitations stemming from mechanical performance degradation and premature fracture failure caused by complex physiological interactions, including flow erosion, corrosion fatigue, stress coupling effects, and dynamic wear under bodily conditions. Surface coating technology has been recognized as an effective strategy to prevent direct contact between magnesium substrates and corrosive media. This review systematically examines the fundamental degradation mechanisms of magnesium alloys in both vivo and vitro environments, presents recent advances in surface modification coatings for magnesium alloys, and critically analyses the interaction mechanisms between modified layers and electrolyte solutions. Special emphasis is placed on revealing the formation mechanisms, structural characteristics, and fracture behaviors of conversion coatings. Furthermore, the study discusses the current challenges in biomedical surface modification of magnesium alloys, proposes potential solutions to enhance their clinical applicability, and outlines future research directions to fully exploit the development potential of these advanced biomaterials.

One of the challenges regarding widespread use of parts made from alloy steel is their time-consuming polishing process. A rough freeform surface of part has been often expected to be polished rapidly up to a smooth surface finish. The focus of this study is to develop a fast polishing method of freeform surface by using dual-beam lasers. The dual-beam laser system consists of continuous laser (CW) and pulsed laser based on a five-axis CNC device. In this study, a series of experiments of CW laser polishing present the effects of different spot irradiation on surface topography, then the combination trajectory of zigzag and square waveform of pulsed laser is explored to realize a “melting peak for filling into valley” (MPFV) method. The polishing experiment on a semisphere of S136H steel polished by dual-beam shows that a rough semisphere surface was rapidly polished from initial state value of Sa (=877 nm) to post-polished value of Sa (=142 nm), and the polishing efficiency is as high as 2890 cm²/H.

As a novel polishing technology, polishing by laser beam radiation can be used to improve the sample surface finish without causing material losses. In order to study the effect of laser polishing on the surface morphology of S136D die steel, an L₁₆(4⁴) orthogonal experiment was designed to describe the variation trend of surface roughness with energy density. The two-dimensional transient model of laser polishing was established to simulate the evolution process of material surface morphology during laser polishing by combining numerical simulation with the experiment. The model uses a moving laser heat source to study the effects of capillary pressure and thermocapillary pressure in the laser polishing process. The experimental results show that the minimum roughness can be reduced to 0.764 μm, and the error between the actual molten pool depth and the simulated molten pool depth is 5.3%.

Laser-based additive manufacturing has garnered significant attention in recent years as a promising 3D-printing method for fabricating metallic components. However, the surface roughness of additive manufactured components has been considered a challenge to achieving high performance. At present, the average surface roughness (Sa) of AM parts can reach high levels, greater than 50 μm, and a maximum distance between the high peaks and the low valleys of more than 300 μm, which requires post machining. Therefore, laser polishing is increasingly being utilized as a method of surface treatment for metal alloys, wherein the rapid remelting and resolidification during the process significantly alter both the surface quality and subsurface material properties. In this paper, the surface roughness, microstructures, microhardness, and wear resistance of the as-received, continuous wave laser polishing (CWLP), and pulsed laser polishing (PLP) processed samples were investigated systematically. The results revealed that the surface roughness (Sa) of the as-received sample was 6.29 μm, which was reduced to 0.94 μm and 0.84 μm by CWLP and PLP processing, respectively. It was also found that a hardened layer, about 200 μm, was produced on the Ti₆Al₄V alloy surface after laser polishing, which can improve the mechanical properties of the component. The microhardness of the laser-polished samples was increased to about 482 HV with an improvement of about 25.2% compared with the as-received Ti₆Al₄V alloy. Moreover, the coefficient of friction (COF) was slightly reduced by both CWLP and LPL processing, and the wear rate of the surface layer was improved to 0.790 mm³/(N∙m) and 0.714 mm³/(N∙m), respectively, under dry fraction conditions.