The poor barrier properties and hygroscopic nature of cellulosic paper impede the wide application of cellulosic paper as a packaging material. Herein, a polyvinyl alcohol (PVA)-based polymer coating was used to improve the barrier performance of paper through its good ability to form a film. Alkyl ketene dimer (AKD) was used to enhance the water resistance. The effect of the absorptive characteristics of the base paper on the barrier properties was explored, and it was shown that surface-sized base paper provides a better barrier performance than unsized base paper. Nanoclay (Cloisite Na⁺) was used in the coating formulation to further enhance the barrier performance. The results show that the coating of PVA/AKD/nanoclay dispersion noticeably improved the barrier performance of the paper. The water vapor transmission rate of the base paper was 533 g/m²·day, and it decreased sharply to 1.3 g/m²·day after the application of a double coating because of the complete coverage of the base paper by the PVA-based polymer coating. The coated paper had excellent water resistance owing to its high water contact angle of around 100°. The grease resistance and mechanical properties of the base paper also improved after coating. This work may provide inspiration for improving the barrier properties of packaging paper through the selection of a suitable base paper and coating formulation.

Due to the micro-sized pores on cellulosic substrate surface and the hygroscopic nature of cellulosic fibers, paper has poor barrier properties. Dispersion coating can improve the barrier properties of cellulosic paper noticeably by forming a continuous, non-porous polymer film on paper surface. In this work, the excellent film-forming performance of polyvinyl alcohol (PVA) was used to seal the surface pores of paper, thus enhancing the barrier properties. Alkyl ketene dimer (AKD) was also added as a coating component to improve the water resistance of paper. Results showed that after PVA/AKD coating hydrophilic base paper changed to hydrophobic one, as proved by water contact angle (WCA) measurements. The water vapor transmission rate (WVTR) of base paper decreased sharply from 543 g/m²·day to 2 g/m²·day in the case of PVA/AKD triple coating, where the threshold of WVTR was reached. Meanwhile, the pristinely non-grease resistant base paper converted to a product with the highest grease resistance level. Furthermore, both elongation at break and tensile strength of base paper improved markedly after PVA/AKD coating. It was concluded that these improved properties were contributed by the combined use of PVA and AKD in the coating.

Coated paper with a porous coating layer may have enhanced light-scattering ability and thus favorable optical properties. However, the increased porosity of such a coating layer is likely to decrease the strength of the coated paper, thereby adversely affecting the quality of the paper in the printing and converting processes. In this research, polymer-stabilized (PS) latex was prepared and used as a cobinder for the pigment coating of the paper. The PS latex particles were colloidally stabilized by a 3:1 mixture of starch and polyvinyl alcohol. The influence of the PS latex cobinder on the viscosity, sedimentation, and consolidation of coating colors was investigated. In addition, the effect of the cobinder on the properties of coating layers, namely, their porosity and surface, optical, and tensile properties, was examined. The results revealed that the PS latex cobinder formed microstructures in the coating colors and affected their viscosity. The addition of PS latex also led to enhanced interactions between coating color components, which affected the consolidation of the coating color, resulting in the formation of dried coating layers with greater porosity and improved optical properties (i.e., higher brightness and opacity) relative to coatings without the PS latex cobinder. Furthermore, the addition of PS latex improved the tensile strength of the coating layers, which was attributable to the small size and the polymeric protective shell of the cobinder particles. Thus, these results show that this PS latex cobinder has the potential to be used for the production of high-quality coated paper products.