Long-term stability in contact with water of organosilane layers formed by octadecyltrimethoxysilane (ODTMS) on polished aluminum alloy (AA2024) through dip-coating was studied by combining SEM, water contact angle measurements, and X-ray photoelectron spectroscopy. Similar organosilane layers were formed on AA2024 coated with permanganate conversion coating, 1,2-bis(triethoxysilyl)ethane (BTSE) and hydrated SiO_x as under-layers, after which their long-term durability was also tested. During immersion in water for about one month, all the samples exhibited a decrease in hydrophobicity, implying the prepared organosilane layer was not stable over time, gradually hydrolyzing and letting water interact with the underlying layer. In parallel, SEM images of one-layer samples taken after immersion showed clear signs of local electrochemical corrosion, while XPS analysis confirmed a loss of silicon from the surface layer. The highest stability over time was demonstrated by a one-layer sample prepared in an ethanol/water bath for 5 min and by a similar ODTMS layer prepared on hydrated MnO_x as an under-layer.

Ultrashort laser pulses deliver electromagnetic energy to matter causing its localized heating that can be used for both material removal via ablation/evaporation and driving interface chemical reactions. Here, it is shown that both mentioned processes can be simultaneously combined within straightforward laser nanotexturing of Si wafer in a functionalizing solution to produce a practically relevant metal–semiconductor surface nano‐morphology. Such unique hybrid morphology represents deep‐subwavelength Si laser‐induced periodic surface structures (LIPSSs) with an extremely short period down to 70 nm and high‐aspect‐ratio nano‐trenches loaded with controllable amount of plasmonic nanoparticles formed via laser‐induced decomposition of the precursor noble‐metal salts. Moreover, heat localization driving reduction process is utilized to produce surface morphology locally decorated with dissimilar plasmon‐active nanoparticles. Light‐absorbing deep‐subwavelength Si LIPSSs loaded with controllable amount of noble‐metal nanoparticles represent an attractive architecture for plasmon‐related applications such as optical nanosensing where efficient coupling of the propagating optical waves to highly localized electromagnetic “hot spots” is a mandatory requirement. To support this statement, applicability of such hybrid morphology for fluorescence‐based detection of nanomolar concentrations of mercury cations in solution is demonstrated.

Combination of dissimilar materials such as noble metals and common semiconductors within unified nanomaterials holds promise for optoelectronics, catalysis and optical sensing. Meanwhile, difficulty of obtaining such hybrid nanomaterials using common lithography-based techniques stimulates an active search for advanced, inexpensive, and straightforward fabrication methods. Here, we report one-pot one-step synthesis of Ag-decorated Si microspheres via nanosecond laser ablation of monocrystalline silicon in isopropanol containing AgNO₃. Laser ablation of bulk silicon creates the suspension of the Si microspheres that host further preferential growth of Ag nanoclusters on their surface upon thermal-induced decomposition of AgNO₃ species by subsequently incident laser pulses. The amount of the AgNO₃ in the working solution controls the density, morphology, and arrangement of the Ag nanoclusters allowing them to achieve strong and uniform decoration of the Si microsphere surface. Such unique morphology makes Ag-decorated Si microspheres promising for molecular identification based on the surface-enhanced Raman scattering (SERS) effect. In particular, the designed single-particles sensing platform was shown to offer temperature-feedback modality as well as SERS signal enhancement up to 10⁶, allowing reliable detection of the adsorbed molecules and tracing their plasmon-driven catalytic transformations. Considering the ability to control the decoration degree of Si microspheres by Ag nanoclusters via amount of the AgNO₃, the developed one-pot easy-to-implement PLAL synthesis holds promise for gram-scale production of high-quality hybrid nanomaterial for various nanophotonics and sensing applications.

The preparation method can considerably affect the structural, morphological, and gas-sensing properties of mixed-oxide materials which often demonstrate superior photocatalytic and sensing performance in comparison with single-metal oxides. In this work, hybrids of semiconductor nanomaterials based on TiO₂ and ZnO were prepared by laser ablation of Zn and Ti plates in water and then tested as chemiresistive gas sensors towards volatile organics (2-propanol, acetaldehyde, ethanol, methanol) and ammonia. An infrared millisecond pulsed laser with energy 2.0 J/pulse and a repetition rate of 5 Hz was applied to Zn and Ti metal targets in different ablation sequences to produce two nano-hybrids (TiO₂/ZnO and ZnO/TiO₂). The surface chemistry, morphology, crystallinity, and phase composition of the prepared hybrids were found to tune their gas-sensing properties. Among all tested gases, sample TiO₂/ZnO showed selectivity to ethanol, while sample ZnO/TiO₂ sensed 2-propanol at room temperature, both with a detection limit of ~50 ppm. The response and recovery times were found to be 24 and 607 s for the TiO₂/ZnO sensor, and 54 and 50 s for its ZnO/TiO₂ counterpart, respectively, towards 100 ppm of the target gas at room temperature.

Here, we present the single-step laser-assisted fabrication of anti-reflective hierarchical surface textures on silicon locally functionalized with a photoluminescent (PL) molecular nanolayer. Using femtosecond-laser ablation of commercial crystalline Si wafers placed under a layer of a solution containing rhodamine 6G (R6G) a triethoxysilyl derivative, we fabricated ordered arrays of microconical protrusions with self-organized nanoscale surface morphology. At the same time, the laser-induced temperature increase facilitated surface activation and local binding of the R6G derivative to the as-fabricated nanotextured surface. The produced dual-scale surface textures showed remarkable broadband (visible to near-IR) light-absorbing properties with an averaged reflectivity of around 1%, and the capping molecular nanolayer demonstrated a strongly enhanced PL yield. By performing a pH sensing test using the produced nanotextured substrate, we confirmed the retention of sensory properties of the molecules attached to the surface and validated the potential applicability of the high-performing liquid-assisted laser processing as a key technology for the development of innovative multifunctional sensing devices in which the textured substrate (e.g., ultra-black semiconductor) plays a dual role as a support and PL signal amplifier.

As the size of the state-of-the-art optical devices shrinks to nanoscale, the need for tools allowing mapping the local optical properties at deep sub-diffraction resolution increases. Here we demonstrate successful mapping the variations of the refractive index of a smooth dielectric surface by detecting spectral response of a single spherical-shape Ag nanoparticle optically aligned with a supporting optical fiber axicon microlens. We propose and examine various excitation schemes of the plasmonic nanoantenna to provide efficient interaction of its dipolar and quadrupolar modes with the underlying sample surface and to optimize the mapping resolution and sensitivity. Moreover, we demonstrate an lithography-free approach for fabrication of the scanning probe combining the high-quality fiber microaxicon with the Ag spherical nanoparticle atop. Supporting finite-difference time-domain calculations are undertaken to tailor the interaction of the plasmonic nanoantenna and the underlying dielectric substrate upon various excitation conditions demonstrating good agreement with our experimental findings and explaining the obtained results.