High-entropy alloy coatings (HEAC) exhibit good frictional wear and corrosion resistances, which are of importance for structure materials. In this study, the microstructure, surface morphology, hardness, frictional wear and corrosion resistance of an AlCoCrFeNi high-entropy alloy coating synthesized by atmospheric plasma spraying (APS) were investigated. The frictional wear and corrosion resistance of the coating are simultaneously improved with an increase of the power of APS. The influence of the APS process on the microstructure and mechanical behavior is elucidated. The mechanisms of frictional wear and corrosion behavior of the AlCoCrFeNi HEAC are discussed in detail.

The structure of Cu₅₀Zr₅₀ and Co₅₆Ta₃₅B₉ metallic glass thin films (MGTF) was effectively tailored via various applied substrate temperatures by means of the magnetron sputtering technology. Obviously enhanced hardness and elastic modulus are achieved by different compositional MGTFs by increasing the substrate temperature. Compared with the CuZr MGTFs, the CoTaB MGTF deposited at 473 K displays the smaller strain-rate sensitivity exponent, m, and a weaker spectrum intensity based on the nanoindentation creep test, suggesting its better creep resistance. In addition, the STZ volume of the CoTaB MGTF significantly decreases after depositing at higher temperature. According to the nano-scratch analysis, the CoTaB MGTF at the substrate temperatures of 473 K performs the shallower scratch width and the larger H³/E² value, indicating its better tribological property.