The extremely high levels of water pollution caused by various industrial activities represent one of the most important environmental problems. Efficient techniques and advanced materials have been extensively developed for the removal of highly toxic organic pollutants, including pesticides. This study investigated the photocatalytic degradation of the fungicide carbendazim (Czm) using composite track-etched membranes (TeMs) in an aqueous solution. Copper(I) oxide (Cu₂O) and zinc oxide (ZnO) microtubes (MTs) were prepared using an electroless template deposition technique in porous poly(ethylene terephthalate) (PET) TeMs with nanochannels with a density of 4 × 10⁷ pores/cm⁻² and diameter of 385 ± 9 nm to yield Cu₂O@PET and ZnO@PET composite membranes, respectively. A mixed Cu₂O/ZnO@PET composite was prepared via a two-step deposition process, containing ZnO (87%) and CuZ (13%) as crystalline phases. The structure and composition of all composite membranes were elucidated using scanning electron microscopy (SEM), atomic force microscopy (AFM), energy-dispersive X-ray spectroscopy (EDS), X-ray photoelectron spectroscopy (XPS) and X-ray diffraction (XRD) techniques. Under UV–visible light irradiation, the Cu₂O/ZnO@PET composite displayed enhanced photocatalytic activity, reaching 98% Czm degradation, higher than Cu₂O@PET and ZnO@PET composites. The maximum Czm degradation efficiency from aqueous solution was obtained at an optimal pH of 6 and contact time of 140 min. The effects of various parameters such as temperature, catalyst dosage and sample exposure time on the photocatalytic degradation process were studied. The degradation reaction of Czm was found to follow the Langmuir–Hinshelwood mechanism and a pseudo-first order kinetic model. The degradation kinetics of Czm accelerated with increasing temperature, and the activation energy (E_a) levels were calculated as 11.9 kJ/mol, 14.22 kJ/mol and 15.82 kJ/mol for Cu₂O/ZnO@PET, ZnO@PET and Cu₂O@PET composite membranes, respectively. The reusability of the Cu₂O/ZnO@PET catalyst was also investigated at different temperatures for 10 consecutive runs, without any activation or regeneration processes. The Cu₂O/ZnO@PET composite exhibited degradation efficiency levels of over 50% at 14 °C and over 30% at 52 °C after 5 consecutive uses.

This paper reports on the synthesis and structure elucidation of track-etched membranes (TeMs) with electrolessly deposited copper microtubes (prepared in etched-only and oxidized polyethylene terephthalate (PET) TeMs), as well as on the comparative testing of arsenic (III) ion removal capacities through bath adsorption experiments. The structure and composition of composites were investigated by X-ray diffraction technique and scanning electron and atomic force microscopies. It was determined that adsorption followed pseudo-second-order kinetics, and the adsorption rate constants were calculated. A comparative study of the applicability of the adsorption models of Langmuir, Freundlich, and Dubinin–Radushkevich was carried out in order to describe the experimental isotherms of the prepared composite TeMs. The constants and parameters of all of the above equations were determined. By comparing the regression coefficients R², it was shown that the Freundlich model describes the experimental data on the adsorption of arsenic through the studied samples better than others. Free energy of As(III) adsorption on the samples was determined using the Dubinin–Radushkevich isotherm model and was found to be 17.2 and 31.6 kJ/mol for Cu/PET and Cu/Ox_PET samples, respectively. The high $E_{Dr}$ value observed for the Cu/Ox_PET composite indicates that the interaction between the adsorbate and the composite is based on chemisorption.

This paper reports the synthesis of composite track-etched membranes (TeMs) modified with electrolessly deposited copper microtubules using copper deposition baths based on environmentally friendly and non-toxic reducing agents (ascorbic acid (Asc), glyoxylic acid (Gly), and dimethylamine borane (DMAB)), and comparative testing of their lead(II) ion removal capacity via batch adsorption experiments. The structure and composition of the composites were investigated by X-ray diffraction technique and scanning electron and atomic force microscopies. The optimal conditions for copper electroless plating were determined. The adsorption kinetics followed a pseudo-second-order kinetic model, which indicates that adsorption is controlled by the chemisorption process. A comparative study was conducted on the applicability of the Langmuir, Freundlich, and Dubinin–Radushkevich adsorption models to define the equilibrium isotherms and the isotherm constants for the prepared composite TeMs. Based on the regression coefficients R², it has been shown that the Freundlich model better describes the experimental data of the composite TeMs on the adsorption of lead(II) ions.

This research examines the features of obtaining composite track-etched membranes based on copper microtubes using various compositions of a deposition solution and various types of reducing agents, such as formaldehyde (Cu_CHOH@PET), dimethylamine borane (Cu_DMAB@PET), glyoxylic acid (Cu_Gly@PET). The structure and composition of the membrane composites were studied by scanning elec-tron microscopy and X-ray phase analysis. It was shown that in the case of using dimethylamine borane as a reducing agent, the obtained composites consisted of copper(I) oxide (37.4 %) and copper(0) (62.6 %), in other cases single-component copper microtubes were obtained. The reduction reaction of chromium(VI) ions was used to evaluate the catalytic ability of prepared composites. It was found that the removal efficiency of chromium ions reached up to 95–97 % in the case of single-component composites; the presence of a cop-per(I) oxide phase in the structure of the Cu_DMAB@PET composites significantly reduced the activity of catalysts and under similar conditions, only 41% of the contaminant was removed from the reaction system. The degradation reaction of Cr(VI) was found to follow the Langmuir-Hinshelwood mechanism and a pseu-do-first-order kinetic model. The calculated value of the reaction rate constant ka for composites of the Cu_DMAB@PET composition (0.017 min–1) was more than 9 times less than that of composites obtained us-ing glyoxylic acid (0.156 min–1) and more than 15 times less than the ka value of Cu_CHOH@PET samples (0.249 min–1). Effect of temperatures on the catalytic ability of composites was studied in the temperature range of 10–38 °C. Some thermodynamic characteristics such as activation energy, enthalpy, and entropy of activation were calculated. It was found that the minimum value of the activation energy was obtained for the Cu_CHOH@PET samples.

The aim of the study is to substantiate the features of active implementation of competence-based chemistry teaching in secondary education institutions of the Republic of Kazakhstan. The methodological approach of the study is based on the following research methods: analysis, synthesis, induction, modelling, comparison, and generalisation. The content of the concept of “competence approach” is defined; its signs and features are revealed, the necessity of introducing the competence approach in the process of teaching chemistry is theoretically proved and the prospects of using the specified approach to improve the study of chemistry among secondary school students of the Republic of Kazakhstan are determined. In the course of theoretical research, the key competences in the process of chemistry teaching, which should be formed in secondary school students of the Republic of Kazakhstan, have been identified. The study identified the contradictions concerning the development of the competence approach in the study of chemistry and outlined ways to solve them. Perspective directions of improvement of competence-based chemistry teaching are defined, and specific recommendations on measures of effective implementation of such an approach in secondary education institutions of the Republic of Kazakhstan are given.