Ti6Al4V samples, obtained by selective laser melting (SLM), were subjected to successive treatments: acid etching, chemical oxidation in hydrogen peroxide solution and thermochemical processing. The effect of temperature and time of acid etching on the surface roughness, morphology, topography and chemical and phase composition after the thermochemical treatment was studied. The surfaces were characterized by scanning electron microscopy, energy dispersive X-ray spectroscopy, X-ray diffraction and contact profilometry. The temperature used in the acid etching had a greater influence on the surface features of the samples than the time. Acid etching provided the original SLM surface with a new topography prior to oxidation and thermochemical treatments. A nanostructure was observed on the surfaces after the full process, both on their protrusions and pores previously formed during the acid etching. After the thermochemical treatment, the samples etched at 40 °C showed macrostructures with additional submicro and nanoscale topographies. When a temperature of 80 °C was used, the presence of micropores and a thicker anatase layer, detectable by X-ray diffraction, were also observed. These surfaces are expected to generate greater levels of bioactivity and high biomechanics fixation of implants as well as better resistance to fatigue.

Ti6Al4V samples obtained by selective laser melting were subjected to acid treatment, chemical oxidation in hydrogen peroxide solution and subsequent thermochemical treatment. The effect of temperature and time of acid etching of Ti6Al4V samples on surface roughness, morphology, topography and chemical and phase composition after the thermochemical treatment was studied. The surfaces were characterized using scanning electron microscopy, energy dispersive X-ray spectroscopy, X-ray diffraction and contact profilometry. Pore and protrusion sizes were measured. Acid etching modified the elemental composition and surface roughness of the alloy. Temperature had a greater influence on the morphology, topography and surface roughness of samples than time. Increases in roughness values were observed when applying successive chemical oxidation and thermochemical treatment compared to the values observed on surfaces with acid etching. After the thermochemical treatment, the samples with acid etching at a temperature of 80 °C showed a multiscale topography. In addition, a network-shaped structure was obtained on all surfaces, both on their protrusions and pores previously formed during the acid etching.