Titanium and its alloys are reference materials in biomedical applications because of their desirable properties. However, one of the most important concerns in long-term prostheses is bone resorption as a result of the stress-shielding phenomena. Development of porous titanium for implants with a low Young’s modulus has accomplished increasing scientific and technological attention. The aim of this study is to evaluate the viability, industrial implementation and potential technology transfer of different powder-metallurgy techniques to obtain porous titanium with stiffness values similar to that exhibited by cortical bone. Porous samples of commercial pure titanium grade-4 were obtained by following both conventional powder metallurgy (PM) and space-holder technique. The conventional PM frontier (Loose-Sintering) was evaluated. Additionally, the technical feasibility of two different space holders (NH₄HCO₃ and NaCl) was investigated. The microstructural and mechanical properties were assessed. Furthermore, the mechanical properties of titanium porous structures with porosities of 40% were studied by Finite Element Method (FEM) and compared with the experimental results. Some important findings are: (i) the optimal parameters for processing routes used to obtain low Young’s modulus values, retaining suitable mechanical strength; (ii) better mechanical response was obtained by using NH₄HCO₃ as space holder; and (iii) Ti matrix hardening when the interconnected porosity was 36–45% of total porosity. Finally, the advantages and limitations of the PM techniques employed, towards an industrial implementation, were discussed.

A great variety of powder metallurgy techniques can produce biomimetic porous titanium structures with similar mechanical properties to host bone tissue. In this work, loose sintering and space holder techniques, two frequently used metallurgical techniques, are compared to evaluate the influences of porosity (content, size, morphology and wall roughness), mechanical properties (stiffness and yield strength) and in-vitro cellular responses (adhesion and proliferation of myoblasts and osteoblasts). These comparisons are made to achieve the best balance between biomechanical and bifunctional behavior of a partial porous implant for cortical bone replacement. Cell adhesion (filopodia presence) and spreading were promoted on both porous surfaces and fully dense substrates (non-porous control surfaces). Porous scaffold samples designed using 50 vol.% NaCl space holder technique had an improved bioactive response over those obtained with the loose sintering technique due to higher roughness and scaffold pore diameter. However, the presence of large and heterogeneous pores compromises the mechanical reliability of the implant. Considering both scenarios, the substrates obtained with 40 vol.% NH₄HCO₃ and pore size ranges between 100 and 200 μm provide a balanced optimization of size and strength to promote in-vitro osseointegration.

The discrepancy between the stiffness of commercially pure titanium and cortical bone tissue compromises its success as a biomaterial. The use of porous titanium has been widely studied, however, it is still challenging to obtain materials able to replicate the porous structure of the bones (content, size, morphology and distribution). In this work, the freeze-casting technique is used to manufacture cylinders with elongated porosity, using a home-made and economical device. The relationship between the processing parameters (diameter and material of the mold, temperature gradient), microstructural features and mechanical properties is established and discussed, in terms of ensuring biomechanical and biofunctional balance. The cylinders have a gradient porosity suitable for use in dentistry, presenting higher Young’s modulus at the bottom, near the cold spot and, therefore better mechanical resistance (it would be in contact with a prosthetic crown), while the opposite side, the hot spot, has bigger, elongated pores and walls.

In the present work, the use of porous titanium is proposed as a solution to the difference in stiffness between the implant and bone tissue, avoiding the bone resorption. Conventional powder metallurgical technique is an industrially established route for fabrication of this type of material. The results are discussed in terms of the influence of compaction pressure and sintering temperature on the porosity (volumetric fraction, size, and morphology) and the quality of the sintering necks. A very good agreement between the predicted values obtained using a simple 2D finite element model, the experimental uniaxial compression behavior, and the analytical model proposed by Nielsen, has been found for both the Young’s modulus and the yield strength. The porous samples obtained by the loose sintering technique and using temperatures between 1000 °C −1100 °C (about 40% of total porosity) are recommended for achieving a suitable biomechanical behavior for cortical bone partial replacement.

Ti6Al4V samples, obtained by selective laser melting (SLM), were subjected to successive treatments: acid etching, chemical oxidation in hydrogen peroxide solution and thermochemical processing. The effect of temperature and time of acid etching on the surface roughness, morphology, topography and chemical and phase composition after the thermochemical treatment was studied. The surfaces were characterized by scanning electron microscopy, energy dispersive X-ray spectroscopy, X-ray diffraction and contact profilometry. The temperature used in the acid etching had a greater influence on the surface features of the samples than the time. Acid etching provided the original SLM surface with a new topography prior to oxidation and thermochemical treatments. A nanostructure was observed on the surfaces after the full process, both on their protrusions and pores previously formed during the acid etching. After the thermochemical treatment, the samples etched at 40 °C showed macrostructures with additional submicro and nanoscale topographies. When a temperature of 80 °C was used, the presence of micropores and a thicker anatase layer, detectable by X-ray diffraction, were also observed. These surfaces are expected to generate greater levels of bioactivity and high biomechanics fixation of implants as well as better resistance to fatigue.