The low-carbon high-Mn austenitic steel microalloyed with titanium was investigated in this work. The steel was solution heat-treated at different temperatures in a range from 900 to 1200 °C. The aim was to receive a different grain size before the static tensile test performed at room temperature. The samples of different grain sizes showed the different strain hardening behavior and resulting mechanical properties. The size of grain diameter below 19 μm was stable up to 1000 °C. Above this temperature, the very enhanced grain growth took place with the grain diameter higher than 220 μm at 1200 °C. This huge grain size at the highest temperature resulted in the premature failure of the sample showing the lowest strength properties at the same time. Correlations between the grain size, the major strengthening mechanism, and fracture behavior were addressed. The relationships were assessed based on microstructural investigations and fractography tests performed for the deformed samples. The best combination of strength and ductility was found for the samples treated at 1000–1100 °C.

Tests were carried out on two high-Mn steels: 27Mn-4Si-2Al-Nb with Nb microaddition and 24Mn-3Si-1.5Al-Nb-Ti with Nb and Ti microadditions. High-manganese austenitic steels, due to their good strength and plastic properties belong to the AHSS (Advanced High-Strength Steel) group and are used in the automotive industry. The main difficulties faced during the casting of the steel and hot working are hot cracks, which can appear in the surface of the ingot. Cracks on the edges of the sheet after hot rolling are the reason for cutting the edges of the sheet and increasing production costs and material losses. The main reason for the formation of hot cracks is the decrease in metal ductility in the high-temperature brittleness range (HTBR). The width of the HTBR depends on mechanical properties and microstructural factors, i.e., non-metallic inclusions or intermetallic phases at austenite grain boundaries. In this paper, a hot tensile test was performed. The research was performed on the GLEEBLE 3800 thermomechanical simulator. This test allows us to determine the width of the high-temperature brittleness range (HTBR), the Nil Strength Temperature (NST), the Nil Ductility Temperature (NDT), and the Ductility Recovery Temperature (DRT). Hot ductility was determined from the value of the reduction in area R(A). The obtained results make it possible to determine the temperature of the beginning of hot working from the tested high-Mn steels. Fractographic research enabled us to define mechanisms of hot cracking. It was found that hot cracks form as a result of disruptions in the liquid film on crystals’ boundaries.

The aim of the work was to determine the effect of Ti micro-addition on the hot tensile behaviour, microstructure and fractography of two low-C high-manganese steels with additions of Si and Al. The hot tensile tests were performed using the Gleeble 3800 thermomechanical simulator. Samples were stretched at a temperature range from 1050 ℃ to 1200 ℃ at a strain rate of 2.5·10 ³ s⁻¹. The microstructure of the tested high-manganese steels under conditions of hot deformation was influenced by strain hardening and simultaneous dynamic recrystallization, as well as precipitation processes-depending on the chemical composition of the alloy and plastic deformation parameters. The analysis of the curves registered in the hot tensile tests indicated that a decrease of strain hardening was the result of the dynamic recrystallization. Hot tensile curves of the Ti-micro-alloyed steel were characterized by higher yield stress compared to the Ti-free steel. The Ti micro-addition with a concentration of 0.075 wt.% guaranteeing stable TiN-type nitrides eliminated the possibility of precipitating AlN-type nitrides and complex MnS-AlN type non-metallic inclusions, which are harmful to hot ductility. Fracture modes of the Ti-free steel showed a mixed nature from 1050 ℃ to 1150 °C, i.e. ductile fracture and numerous cavities and voids were identified. As the deformation temperature increased to 1200 °C, the fracture character was brittle with numerous inter-crystalline cracks along austenite grain boundaries. The addition of Ti improved significantly the hot ductility behaviour characterized by higher values of flow stress and reduction in area as well as ductile fracture modes in the entire high deformation temperature range.

The work presents the results of research on the effect of deformation parameters on hot ductility of high-Mn austenitic steel with niobium and titanium. The investigations were carried out on steel with 0.05% C, 24% Mn, 3.5% Si, 1.5% Al, 0.030% Nb and 0.075% Ti. Hot static tensile test was...

The aim of the work was to determine the effect of non-metallic inclusions on the hot ductility of two newly developed high-Mn austenitic steels (27Mn-4Si-2Al and 24Mn-3Si-1.5Al-Ti). For this purpose, a hot tensile test was carried out in the temperature range from 1050°C to 1200°C with a...