The low-carbon high-Mn austenitic steel microalloyed with titanium was investigated in this work. The steel was solution heat-treated at different temperatures in a range from 900 to 1200 °C. The aim was to receive a different grain size before the static tensile test performed at room temperature. The samples of different grain sizes showed the different strain hardening behavior and resulting mechanical properties. The size of grain diameter below 19 μm was stable up to 1000 °C. Above this temperature, the very enhanced grain growth took place with the grain diameter higher than 220 μm at 1200 °C. This huge grain size at the highest temperature resulted in the premature failure of the sample showing the lowest strength properties at the same time. Correlations between the grain size, the major strengthening mechanism, and fracture behavior were addressed. The relationships were assessed based on microstructural investigations and fractography tests performed for the deformed samples. The best combination of strength and ductility was found for the samples treated at 1000–1100 °C.

Modification of Non-Metallic Inclusions by Rare-Earth Elements in Microalloyed Steels: The modification of the chemical composition of non-metallic inclusions by rare-earth elements in the new-developed microalloyed steels was discussed in the paper. The investigated steels are assigned to production of forged elements by thermo-mechanical treatment. The steels were melted in a vaccum induction furnace and modification of non-metallic inclusions was carried out by the michmetal in the amount of 2.0 g per 1 kg of steel. It was found that using material charge of high purity and a realization of metallurgical process in vacuous conditions result in a low concentration of sulfur (0.004%), phosphorus (from 0.006 to 0.008%) and oxygen (6 ppm). The high metallurgical purity is confirmed by a small fraction of non-metallic inclusions averaging 0.075%. A large majority of non-metallic inclusions are fine, globular oxide-sulfide or sulfide particles with a mean size 17 μm². The chemical composition and morphology of non-metallic inclusions was modified by Ce, La and Nd, what results a small deformability of non-metallic inclusions during hot-working.

The work presents results of phase transformation kinetics of hot-rolled 5% Mn steel subjected to different heat treatments. Three different schedules were introduced: isothermal holding in a bainite region, coiling simulation and intercritical annealing. The evolution of microstructure components was investigated using dilatometric and metallographic analyses. According to obtained results, the medium-Mn steel exhibits high resistance for γ/α transformation during the bainite transformation and coiling simulation (upon cooling from the austenite region). During 5 h isothermal holding, no bainite and/or ferrite formation was detected. This results in the formation of martensite upon cooling to room temperature. Differently, when the steel was subjected to the intercritical annealing at 720 and 700 °C (upon heating from room temperature), a final microstructure consisted of ferrite, martensite and retained austenite. At 700 °C, no fresh martensite formation was detected upon cooling to room temperature. This means that the austenite was enriched in carbon during the intercritical annealing step enough to keep its thermal stability.

The paper presents the investigation results of the impact of shear bands on microstructure, mechanical properties, and anisotropy of plastic properties of HSLA (high-strength, low-alloy) type steel plates, produced in the process of thermomechanical rolling. A lack of conditions ensuring the complete static recrystallization between successive roll passes leads to localization of plastic deformation and formation of shear bands in dynamically-recrystallized austenite enriched with carbon and other interstitial elements, which transform into carbide segregation bands during tempering. These bands are the cause of low impact resistance of rolled plates, especially in the transverse direction, and the high degree of anisotropy of plastic properties in the plates.