In this work, the effects of graphene oxide (GO) concentrations (1.5 wt.%, 2.5 wt.%, and 5 wt.%) on the structural, morphological, optical, and luminescence properties of zinc oxide nanorods (ZnO NRs)/GO nanocomposites, synthesized by a facile hydrothermal process, were investigated. X-ray diffraction (XRD) patterns of NRs revealed the hexagonal wurtzite structure for all composites with an average coherence length of about 40–60 nm. A scanning electron microscopy (SEM) study confirmed the presence of transparent and wrinkled, dense GO nanosheets among flower-like ZnO nanorods, depending on the GO amounts used in preparation. Raman spectroscopy, Fourier transform infrared spectroscopy (FTIR), ultraviolet–visible (UV–Vis) absorption spectroscopy, and photoluminescence (PL) measurements revealed the impact of GO concentration on the optical and luminescence properties of ZnO NRs/GO nanocomposites. The energy band gap of the ZnO nanorods was independent of GO concentration. Photoluminescence spectra of nanocomposites showed a significant decrease in the intensities in the visible light range and red shifted suggesting a charge transfer process. The nanocomposites’ chromaticity coordinates for CIE 1931 color space were estimated to be (0.33, 0.34), close to pure white ones. The obtained results highlight the possibility of using these nanocomposites to achieve good performance and suitability for optoelectronic applications.

TiO₂–SiO₂ nanocomposite thin films have gained the attention of the scientific community due to their unique physical and chemical properties. In this paper, we report on the fabrication and characterization of a TiO₂–SiO₂ nanocomposite disk-shaped target. The target was used for the deposition of TiO₂–SiO₂ nanocomposite thin films on fluorine-doped tin oxide/glass substrates using the pulsed laser deposition (PLD) technique. The thicknesses of the thin films were fixed to 100 nm, and the deposition temperature ranged from room temperature to 300 °C. As revealed by the microstructural and morphological characterizations revealed, the TiO₂–SiO₂ nanocomposite thin films are amorphous and display homogeneous distribution. The determined values of the indirect optical band gap range from 2.92 to 3.07 eV, while those of the direct optical band gap lie between 3.50 and 3.55 eV. Additionally, as the deposition temperature decreases, the light transmission increases in the visible and in the ultraviolet ranges, which is suitable for flexible perovskite solar cells. This research can uncover new insights into the fabrication of amorphous TiO₂–SiO₂-based nanostructured thin films using the PLD technique for perovskite solar cell technology.