In this article, the effect of plasma treatment of polyethylene powder and glass fibers on the adhesion between polyethylene and glass fibers in composites prepared by rotational molding was studied. In contrast to other processing techniques, such as injection molding, the rotational molding process operates at atmospheric pressure, and no pressure is added to ensure mechanical interlocking. This makes reinforcing the rotomolded product very difficult. Therefore, the formation of chemical bonds is necessary for strong adhesion. Different combinations of untreated polyethylene (UT.PE), plasma-treated polyethylene (PT.PE), untreated and plasma-treated glass fibers were manually mixed and processed by rotational molding. The resulting composites were cut and tested to demonstrate the effect of the treatment on the adhesion between the composite components and on the mechanical properties of the final composites. The results showed that the treatment of both powder and fiber improved the adhesion between the matrix and fibers, thus improving the mechanical properties of the resulting composites compared to those of pure polyethylene samples and composites prepared using untreated components. The tensile strength, tensile modulus, and flexural modulus of the composites prepared using 10-min treated powder with 20 wt% of 40-min treated fibers improved by 20%, 82%, and 98%, respectively, compared to the pure polyethylene samples.

Rotational molding is a manufacturing technique for producing 3D hollow parts by adding plastic powder to a shell-like mold and rotating the mold while heating it with the powder. In contrary to the injection molding all the process operates at atmospheric pressure which makes reinforcement of the rotomolded product difficult. In this paper plasma treated PE and short glass fibers were dry mixed and used to produce composites by rotational molding process and characterized in terms of morphology and mechanical properties.