In the last few years, high-entropy oxides (HEOs), a new class of single-phase solid solution materials, have attracted growing interest in both academic research and industry for their great potential in a broad range of applications. This work investigates the possibility of producing pure single-phase HEOs with spinel structure (HESOs) under milder conditions (shorter heat treatments at lower temperatures) than standard solid-state techniques, thus reducing the environmental impact. For this purpose, a large set of HESOs was prepared via sol-gel and electrospinning (by using two different polymers). Ten different equimolar combinations of five metals were considered, and the influence of the synthesis method and conditions on the microstructure, morphology and crystalline phase purity of the produced HESOs was investigated by a combination of characterization techniques. On the other hand, the presence of specific metals, such as copper, lead to the formation of minority secondary phase(s). Finally, two representative pure single-phase HESOs were preliminarily evaluated as active anode materials in lithium-ion batteries and possible strategies to enhance their rate capability and cyclability were proposed and successfully implemented. The approaches introduced here can be extensively applied for the optimization of HEO properties targeting different applications.

Haematite ( α -Fe ₂ O ₃ ) nanostructures were synthesized via a Pechini sol–gel method (PSG) and an electrospinning (ES) technique. Their texture and morphology were investigated by scanning and transmission electron microscopy. α -Fe ₂ O ₃ nanoparticles were obtained by the PSG method, whereas fibrous structures consisting of interconnected particles were synthesized through the ES technique. The crystallinity of the α -Fe ₂ O ₃ nanostructures was also studied by means of x-ray diffraction and Raman spectroscopy. Gas-sensing devices were fabricated by printing the synthesized samples on ceramic substrates provided with interdigitated Pt electrodes. The sensors were tested towards low concentrations of ethanol in air in the temperature range (200−400°C). The results show that the α -Fe ₂ O ₃ nanostructures exhibit somewhat different gas-sensing properties and, interestingly, their sensing behaviour is strongly temperature-dependent. The availability of active sites for oxygen chemisorption and the diffusion of the analyte gas within the sensing layer structure are hypothesized to be the key factors responsible for the different sensing behaviour observed.