This review aims to consolidate scattered literature on thermally sprayed coatings with nonionizing electromagnetic (EM) wave absorption and shielding over specific wavelengths potentially useful in diverse applications (e.g., microwave to millimeter wave, solar selective, photocatalytic, interference shielding, thermal barrier‐heat/emissivity). Materials EM properties such as electric permittivity, magnetic permeability, electrical conductivity, and dielectric loss are critical due to which a material can respond to absorbed, reflected, transmitted, or may excite surface electromagnetic waves at frequencies typical of electromagnetic radiations. Thermal spraying is a standard industrial practice used for depositing coatings where the sprayed layer is formed by successive impact of fully or partially molten droplets/particles of a material exposed to high or moderate temperatures and velocities. However, as an emerging novel application of an existing thermal spray techniques, some special considerations are warranted for targeted development involving relevant characterization. Key potential research areas of development relating to material selection and coating fabrication strategies and their impact on existing practices in the field are identified. The study shows a research gap in the feedstock materials design and doping, and their complex selection covered by thermally sprayed coatings that can be critical to advancing applications exploiting their electromagnetic properties.

The mechanisms of nanoscale fatigue of functionally graded TiN/TiNi films have been studied using multiple-loading cycle nanoindentation and nano-impact tests. The functionally graded films were sputter deposited onto silicon substrates, in which the TiNi film provides pseudo-elasticity and shape memory behaviour, while a top TiN surface layer provides tribological and anti-corrosion properties. Nanomechanical tests were performed to investigate the localised film performance and failure modes of the functionally graded film using both Berkovich and conical indenters with loads between 100 μN and 500 mN. The loading history was critical to define film failure modes (i.e. backward depth deviation) and the pseudo-elastic/shape memory effect of the functionally graded layer. The results were sensitive to the applied load, loading mode (e.g. semi-static, dynamic) and probe geometry. Based on indentation force–depth profiles, depth–time data and post-test surface observations of films, it was concluded that the shape of the indenter is critical to induce localised indentation stress and film failure, and generation of pseudo-elasticity at a lower load range. Finite-element simulation of the elastic loading process indicated that the location of subsurface maximum stress near the interface influences the backward depth deviation type of film failure.

Thermal spray coatings have the advantage of providing thick and functional coatings from a range of engineering materials. The associated coating processes provide good control of coating thickness, morphology, microstructure, pore size and porosity, and residual strain in the coatings through selection of suitable process parameters for any coating material of interest. This review consolidates scarce literature on thermally sprayed components which are critical and vital constituents (e. g., catalysts (anode/cathode), solid electrolyte, and transport layer, including corrosion‐prone parts such as bipolar plates) of the water splitting electrolysis process for hydrogen production. The research shows that there is a gap in thermally sprayed feedstock material selection strategy as well as in addressing modelling needs that can be crucial to advancing applications exploiting their catalytic and corrosion‐resistant properties to split water for hydrogen production. Due to readily scalable production enabled by thermal spray techniques, this manufacturing route bears potential to dominate the sustainable electrolyser technologies in the future. While the well‐established thermal spray coating variants may have certain limitations in the manner they are currently practiced, deployment of both conventional and novel thermal spray approaches (suspension, solution, hybrid) is clearly promising for targeted development of electrolysers.

Detecting and monitoring of corrosion is one of the major challenges in insulated metallic structures or structures with one or more than one interface. This review paper aims to consolidate scattered literature on laboratory system-based corrosion measurement at the interface region. There are range of sensor-based detection and monitoring methods (active, passive) for corrosion rate analysis, including those which measures a surrogate, i.e. quantifying moisture, temperature, pH and qualify other changes or degradations at the interface. With the emergence of a novel application of advanced sensing methods, this review also presents the possibility of the application of hybrid and multifunctional sensing methods at the interfaces, aimed at advancing corrosion monitoring at the interface region. Key research areas of development relating to the application of combination of other materials (e.g. metal oxides, carbon nanotubes, metal nanowires, piezoelectric) as potential sensors and their impact on existing practices in the field are identified. GRAPHICAL ABSTRACT

Failure behaviour of two types of adhesively bonded joints (composite-to-metal, metal-to-metal) has been studied under failure modes (Mode I: double cantilever beam (DCB) and Mode II: three-point end notch flexures (3-ENF)) using acoustic emission (AE) technique. The bonded specimens were prepared using two types of adhesive bond materials with three variations of adhesive bond quality. The effect of the presence of interfacial defects along the interface on the residual strength of the joint has also been studied. It was possible using the maximum AE amplitude method to select the AE events of mechanical significance. However, it proved difficult to propose a definitive AE trait for the mechanical phenomena occurring within specific AE event signals, for all adhesive types, bond qualities, and substrate configurations, therefore, all specimen combinations. There was a notable shift in spectral energy proportion as the AE source of mechanical significance varied along the specimen length for specimen combinations. However, it was difficult to confirm this distinctive trait for all specimen combinations due to difficulty in confirming the location and exact mechanical source. The proposed measurement technique can be useful to assess the overall structural health of a bonded system and may allow identification of defects.