The possibility of tuning magnetic material properties by ionic means is exciting both for basic science and, especially in view of the excellent energy efficiency and room temperature operation, for potential applications. In this perspective, we shortly introduce the functionality of magneto-ionic materials and focus on important recent advances in this field. We present a comparative overview of state-of-the-art magneto-ionic materials considering the achieved magnetoelectric voltage coefficients for magnetization and coercivity and the demonstrated time scales for magneto-ionic switching. Furthermore, the application perspectives of magneto-ionic materials in data storage and computing, magnetic actuation, and sensing are evaluated. Finally, we propose potential research directions to push this field forward and tackle the challenges related to future applications.

The effect of microstructure on the efficiency of shielding or shunting of the magnetic flux by permalloy shields was investigated in the present work. For this purpose, the FeNi shielding coatings with different grain structures were obtained using stationary and pulsed electrodeposition. The coatings’ composition, crystal structure, surface microstructure, magnetic domain structure, and shielding efficiency were studied. It has been shown that coatings with 0.2–0.6 µm grains have a disordered domain structure. Consequently, a higher value of the shielding efficiency was achieved, but the working range was too limited. The reason for this is probably the hindered movement of the domain boundaries. Samples with nanosized grains have an ordered two-domain magnetic structure with a permissible partial transition to a superparamagnetic state in regions with a grain size of less than 100 nm. The ordered magnetic structure, the small size of the domain, and the coexistence of ferromagnetic and superparamagnetic regions, although they reduce the maximum value of the shielding efficiency, significantly expand the working range in the nanostructured permalloy shielding coatings. As a result, a dependence between the grain and domain structure and the efficiency of magnetostatic shielding was found.

The results of research on the behavior of Ni nanotubes under the influence of environments with different pH values are presented. The influence of exposure time on morphology and composition under specific test conditions was investigated, and a detailed study of the nanotube crystal structure parameters vs. time was carried out. Based on the obtained results, a mechanism for the degradation of Ni nanotubes under different conditions was suggested.