Binary and ternary composites (CM) based on M-type hexaferrite (HF), polymer matrix (PVDF) and carbon nanomaterials (quasi-one-dimensional carbon nanotubes—CNT and quasi-two-dimensional carbon nanoflakes—CNF) were prepared and investigated for establishing the impact of the different nanosized carbon on magnetic and electrodynamic properties. The ratio between HF and PVDF in HF + PVDF composite was fixed (85 wt% HF and 15 wt% PVDF). The concentration of CNT and CNF in CM was fixed (5 wt% from total HF + PVDF weight). The phase composition and microstructural features were investigated using XRD and SEM, respectively. It was observed that CM contains single-phase HF, γ- and β-PVDF and carbon nanomaterials. Thus, we produced composites that consist of mixed different phases (organic insulator matrix—PDVF; functional magnetic fillers—HF and highly electroconductive additives—CNT/CNF) in the required ratio. VSM data demonstrate that the main contribution in main magnetic characteristics belongs to magnetic fillers (HF). The principal difference in magnetic and electrodynamic properties was shown for CNT- and CNF-based composites. That confirms that the shape of nanosized carbon nanomaterials impact on physical properties of the ternary composited-based magnetic fillers in polymer dielectric matrix.

Magnetic Fe₃O₄ nanoparticles (NPs) and their surface modification with therapeutic substances are of great interest, especially drug delivery for cancer therapy, including boron-neutron capture therapy (BNCT). In this paper, we present the results of boron-rich compound (carborane borate) attachment to previously aminated by (3-aminopropyl)-trimethoxysilane (APTMS) iron oxide NPs. Fourier transform infrared spectroscopy with Attenuated total reflectance accessory (ATR-FTIR) and energy-dispersive X-ray analysis confirmed the change of the element content of NPs after modification and formation of new bonds between Fe₃O₄ NPs and the attached molecules. Transmission (TEM) and scanning electron microscopy (SEM) showed Fe₃O₄ NPs’ average size of 18.9 nm. Phase parameters were studied by powder X-ray diffraction (XRD), and the magnetic behavior of Fe₃O₄ NPs was elucidated by Mössbauer spectroscopy. The colloidal and chemical stability of NPs was studied using simulated body fluid (phosphate buffer—PBS). Modified NPs have shown excellent stability in PBS (pH = 7.4), characterized by XRD, Mössbauer spectroscopy, and dynamic light scattering (DLS). Biocompatibility was evaluated in-vitro using cultured mouse embryonic fibroblasts (MEFs). The results show us an increasing of IC₅₀ from 0.110 mg/mL for Fe₃O₄ NPs to 0.405 mg/mL for Fe₃O₄-Carborane NPs. The obtained data confirm the biocompatibility and stability of synthesized NPs and the potential to use them in BNCT.

Nanostructured NiFe film was obtained on silicon with a thin gold sublayer via pulsed electrodeposition and annealed at a temperature from 100 to 400 °C in order to study the effect of heat treatment on the surface microstructure and mechanical properties. High-resolution atomic force microscopy made it possible to trace stepwise evolving microstructure under the influence of heat treatment. It was found that NiFe film grains undergo coalescence twice—at ~100 and ~300 °C—in the process of a gradual increase in grain size. The mechanical properties of the Au/NiFe nanostructured system have been investigated by nanoindentation at two various indentation depths, 10 and 50 nm. The results showed the opposite effect of heat treatment on the mechanical properties in the near-surface layer and in the material volume. Surface homogenization in combination with oxidation activation leads to abnormal strengthening and hardening-up of the near-surface layer. At the same time, a nonlinear decrease in hardness and Young’s modulus with increasing temperature of heat treatment characterizes the internal volume of nanostructured NiFe. An explanation of this phenomenon was found in the complex effect of changing the ratio of grain volume/grain boundaries and increasing the concentration of thermally activated diffuse gold atoms from the sublayer to the NiFe film.

Due to the Ni nanotubes’ shape anisotropy, low specific density, large specific surface, and uniform magnetic field, they have been offered as carriers for targeted delivery of drug or protein and the process of their formation from synthesis stage to the stage of surface modification and protein attaching has been demonstrated. Some steps to hasten their biomedical application have been applied. First, to have full control over the carrier dimensions and structure parameters, electrodeposition method in pores of polyethylene terephthalate template has been applied. Second, to understand the scope of Ni nanostructures application, their degradation in media with different acidity has been studied. Third, to improve the biocompatibility and to make payloads attachment possible, nanotubes surface modification with organosilicon compound has been carried out. At last, the scheme of protein attaching to the nanostructure surface has been developed and the binding process was demonstrated as an example of the bovine serum albumin.

A comprehensive study of parameters of the track membranes based on the polyethylene terephthalate has been carried out at different formation stages. Usin

Surface-enhanced Raman spectroscopy (SERS) is a promising optical method for analyzing molecular samples of various nature. Most SERS studies are of an applied nature, indicating a serious potential for their application in analytical practice. Dendritelike nanostructures have great potential for SERS, but the lack of a method for their predictable production significantly limits their implementation. In this paper, a method for controllably obtaining spatially separated, self-organized, and highly-branched silver dendrites via template synthesis in pores of SiO₂/Si is proposed. The dendritic branches have nanoscale roughness, creating many plasmon-active “hotspots” required for SERS. The first held 3D modeling of the external electromagnetic wave interaction with such a dendrite, as well as experimental data, confirms this theory. Using the example of a reference biological analyte, which is usually used as a label for other biological molecules, the dendrites’ SERS-sensitivity up to 10⁻¹⁵M was demonstrated with an enhancement factor of 10⁸. The comparison of simulation results with SERS experiments allows distinguishing the presence of electromagnetic and chemical contributions, which have a different effect at various analyte concentrations.