Control of the homogenization process is important in obtaining high extrudability and desirable properties in 6xxx aluminum alloys. Three consecutive steps of the process chain were modeled. Microsegregation arising from solidification was described with the Scheil–Gulliver model. Dissolution of Mg₂Si, Si (diamond) and β-AlFeSi (β-Al₅FeSi) to α-AlFeSi (α-Al₁₂(FeMn)₃Si) transformation during homogenization have been described with a CALPHAD-based multicomponent diffusion Dual-Grain Model (DGM), accounting for grain size inhomogeneity. Mg₂Si precipitation and associated strengthening during homogenization cooling were modeled with the Kampmann–Wagner Numerical (KWN) precipitation framework. The DGM model indicated that the fractions of β-AlFeSi and α-AlFeSi exhibit an exact spatial and temporal correspondence during transformation. The predictions are in good agreement with experimental data. The KWN model indicated the development of a bimodal particle size distribution during homogenization cooling, arising from corresponding nucleation events. The associated strengthening, arising from solid solution and precipitation strengthening, was in good agreement with experimental results. The proposed modeling approach is a valuable tool for the prediction of microstructure evolution during the homogenization of 6xxx aluminum alloys, including the often-neglected part of homogenization cooling.

High silicon and molybdenum ductile cast irons (Si-Mo alloys) are commonly used as exhaust manifold materials suffering from high temperature-oxidation and thermal-mechanical fatigue. The structural integrity of cast Si-Mo alloys under these service conditions is attributed to their microstructure consisting of spheroidal graphite and Mo-rich carbide embedded in a ferritic matrix. However, the cast structure includes also pearlite structure having a detrimental effect on the mechanical properties, therefore the cast matrix needs to be heat treated. In this study, the solidification of a Si-Mo ductile iron was investigated using (i) thermodynamic and kinetic calculations by Thermo-Calc and DICTRA software and (ii) thermal analysis in order to reveal out the sequence of phase formation and the phase transformations during solidification and (iii) microanalysis by energy dispersive spectrometer in order to determine elemental segregation and compare with the calculated values. The solidified structure was also characterized and all microstructural features were specified.

Desirable properties including strength, ductility and extrudability of 6060 Al-alloys are highly dependent on processing to control the development of microstructural features. In this study, the process chain of an extrudable 6060 Al-alloy was modeled in an Integrated Computational Materials Engineering framework and validated experimentally via quantitative SEM-EDX and TEM. All critical processing stages were considered including casting, homogenization heating and holding, extrusion cooling and two-stage aging. Segregation and intermetallics formation were accurately predicted and experimentally verified in the as-cast condition. Diffusion simulations predicted the dissolution of intermetallics and completion of β-AlFeSi to α-AlFeSi transformation during homogenization, in excellent agreement with quantitative SEM-EDX characterization. Precipitation simulations predicted the development of a β″ strengthening dispersion during extrusion cooling and aging. Needle-shaped β″ precipitates were observed and analyzed with quantitative high-resolution TEM, validating predictions. Ensuing precipitation strengthening was modeled in terms of aging time, presenting good agreement with yield strength measurements. Precipitate-Free Zones and coarse, metastable β-type particles on dispersoids and grain boundaries were investigated. The proposed integrated modeling and characterization approach considers all critical processing stages and could be used to optimize processing of extrudable 6xxx Al-alloys, providing insight to mechanisms controlling microstructural evolution and resulting properties.

Extrudability of aluminum alloys of the 6xxx series is highly dependent on the microstructure of the homogenized billets. It is therefore very important to characterize quantitatively the state of homogenization of the as-cast billets. The quantification of the homogenization state was based on the measurement of specific microstructural indices, which describe the size and shape of the intermetallics and indicate the state of homogenization. The indices evaluated were the following: aspect ratio (AR), which is the ratio of the maximum to the minimum diameter of the particles, feret (F), which is the maximum caliper length, and circularity (C), which is a measure of how closely a particle resembles a circle in a 2D metallographic section. The method included extensive metallographic work and the measurement of a large number of particles, including a statistical analysis, in order to investigate the effect of homogenization time. Among the indices examined, the circularity index exhibited the most consistent variation with homogenization time. The lowest value of the circularity index coincided with the metallographic observation for necklace formation. Shorter homogenization times resulted in intermediate homogenization stages involving rounding of edges or particle pinching. The results indicated that the index-based quantification of the homogenization state could provide a credible method for the selection of homogenization process parameters towards enhanced extrudability.