Polymer infiltrated ceramic network (PICN) composites are an increasingly popular dental restorative material that offer mechanical biocompatibility with human enamel. This study aimed to develop a novel PICN composite as a computer-aided design and computer-aided manufacturing (CAD/CAM) block for dental applications. Several PICN composites were prepared under varying conditions via the sintering of a green body prepared from a silica-containing precursor solution, followed by resin infiltration. The flexural strength of the PICN composite block (107.8–153.7 MPa) was similar to a commercial resin-based composite, while the Vickers hardness (204.8–299.2) and flexural modulus (13.0–22.2 GPa) were similar to human enamel and dentin, respectively. The shear bond strength and surface free energy of the composite were higher than those of the commercial resin composites. Scanning electron microscopy and energy dispersive X-ray spectroscopic analysis revealed that the microstructure of the composite consisted of a nanosized silica skeleton and infiltrated resin. The PICN nanocomposite block was successfully used to fabricate a dental crown and core via the CAD/CAM milling process.

SiO₂-poly(2-hydroxyethyl methacrylate) (pHEMA)-based composites have been widely used as biomaterials owing to their biocompatibility. However, they have not yet been applied as tooth restorative materials because of their poor mechanical properties. In the present paper, we develop a novel SiO₂/pHEMA-based composite with a polymer-infiltrated network (PICN) structure for use in dental restorative materials. A mixture of SiO₂ nanoparticles and a poly(vinyl alcohol) binder was sintered at 950 °C to fabricate a porous SiO₂ block. A monomer mixture containing 70 wt%-HEMA/30 wt%-ethylene glycol dimethacrylate and a benzoyl peroxide initiator was infiltrated into the porous SiO₂ block and heat-polymerized to fabricate the SiO₂/pHEMA-based composite with a PICN structure. The composite was characterized according to its mechanical properties, surface free energy, and bonding properties with a dental adhesive. The flexural strength was 112.5 ± 18.7 MPa, the flexural modulus was 13.6 ± 3.4 GPa, and the Vickers hardness was 168.2 ± 16.1, which are similar values to human teeth. The surface free energy of the polar component of the composite was 19.6 ± 2.5 mN/m, suggesting that this composite has an active surface for bonding with the adhesive. The composite bonded well to the adhesive, in the presence of a silane coupling agent. The SiO₂/pHEMA-based composite was demonstrated to be a potential candidate for dental restorative materials.