Thionocarbamates are the group of collectors that are mostly used for flotation of sulphide copper minerals, alone or in combination with xanthates depending on a mineralogical composition of the ore. In this paper, the results of the study of application of thionocarbamates in copper slag flotation are presented. Chemical analysis of smelter slag sample obtained from Flotation plant in Bor, Serbia, showed that it contains 3.56% of copper, of which over 73% is in the sulphide form, as well as 0.58 g/t of gold and 11.30 g/t of silver. XRD analysis identified fayalite and magnetite as main minerals present in the slag and SEM-EDS analysis showed that copper is mainly present in the form of sulphide minerals, thus making it suitable for flotation with thionocarbamates. Two thionocarbamates MX 980 and TC 1000 and one xanthate SIPX, along with their mixtures MX 980 + SIPX and TC 1000 + SIPX, were investigated. The influence of parameters such as collector type and dosage, grinding fineness, pulps’ pH and flotation time, on flotation indicators (recovery, yield and copper grade in concentrate) were determined. Smaller dosages of thionocarbamates (40 g/t) provided concentrates with high copper grades, 22.34% (MX 980) and 18.42% (TC 1000) and lower recovery rates, 83.98% (MX 980) and 87.78% (TC 1000), while the increase of dosages to 200 g/t led to the increase of recovery rates for more than 4% and a significant decrease in copper grades. The increase of grinding fineness from 50% to 70% of grain size < 0.074 mm showed a positive impact on flotation indicators, recovery rate, copper grade and yield, for all investigated collectors and their mixtures, while, with the further increase from 70% to 90%, recovery rates continued to increase while copper grades decreased. The increase of pulps’ pH had a positive influence, especially for MX 980, for which recovery rates increased with the increase of pH from 8 to 10 (12). A flotation kinetics test showed that flotation with TC 1000 was the fastest, i.e., recovery rate after 20 min of flotation was over 91%, while recoveries obtained with other collectors were a few percentage points lower.

Flotation of grinding products with 55, 60, 65, 70, and 75% of grain size <74 μm, was conducted at the pulp’s pH values of 10 and 12. Higher copper recovery was obtained in concentrates at pH 10, but with lower copper grades, approximately 2%. Copper recovery in concentrates at pH 12 was slightly less, but copper grades were much higher. The effect of grinding was higher at pH 12, especially in terms of copper grades in concentrates, which declined with the increase of grinding time. Ore microscopy tests were done on the concentrates with 55 and 75% of grain size <74 μm at pH 10 and 12. All particles of copper minerals were divided by grain size fractions and by the degree of liberation. Analysis have shown that degree of liberation was higher in finer grinding products.

This paper considers the impact of copper mining-influenced water and metallurgical wastewater on the surface water in the Bor area, Serbia. Sampling, realized through the four campaigns (2020–2021), confirmed that both types of water, discharged without appropriate treatment in the Bor River, had a signific impact on the concentration of metal ions, pH and electrical conductivity on the watercourse in the Bor area. The highest concentrations of the following metal ions, Cu—271 mg/L, As—25,991 μg/L, Ni—13,856 μg/L, Cd—2627 μg/L, and Pb—2855 μg/L, were registered in the metallurgical wastewater samples. After changes occurred in the copper production process by stopping the discharge of untreated wastewater into the Bor River, the concentrations of monitored elements were drastically decreased. In the period 2022–2024, the concentration values for Cu, As and Pb ions were below the maximum allowable value, and the concentration values of Ni and Cd ions were also decreased. The values for pH and electrical conductivity were in the maximum allowable range. The return of wastewater to the copper production process would lead to both a reduction in the primary water consumption and reduction in the negative impact on the environment.

This paper presents the results of mineralogical and flotation studies on the copper ore from the deposit "North Revir" in the Copper Mine Majdanpek, using different collectors. XRD and ore mineralogical analysis showed that the most common minerals are pyrite and chalcopyrite. Chemical analysis confirm that it is a complex low-grade copper ore with average copper content of 0,273%. The content of precious metals (Au and Ag) was 0.2 g/t and 1.2 g/t, respectively. The main aim of flotation studies have been the effect of collector type on the recovery and concentrate grade in the copper flotation process. Various collectors and combinations of them were used in the rough flotation tests of copper ore. The copper recovery was in the range from 79.43% (test no. 4) to 84.96% (test no. 7). The best flotation results were obtained with mixture collectors of sodium isopropyl xanthate (Z11), dialkyl dithiophosphinates (Aerophine 3404) and SKIK BZ 2000. The collector's dosages of 20 g/t Z11, 8 g/t AP3404 and 8 g/t SKIK BZ 2000 produced the copper recovery (84.96 %) with copper concentrate grade of 1.52% .