A structural study of epoxidized natural rubber (ENR-50) and its cyclic dithiocarbonate derivative was carried out using NMR spectroscopy techniques. The overlapping ¹H-NMR signals of ENR-50 at δ 1.56, 1.68–1.70, 2.06, 2.15–2.17 ppm were successfully assigned. In this work, the ¹³C-NMR chemical shift assignments of ENR-50 were consistent to the previously reported work. A cyclic dithiocarbonate derivative of ENR-50 was synthesized from the reaction of purified ENR-50 with carbon disulfide (CS₂), in the presence of 4-dimethylaminopyridine (DMAP) as catalyst at reflux temperature. The cyclic dithiocarbonate formation involved the epoxide ring opening of the ENR-50. This was followed by insertion of the C–S moiety of CS₂ at the oxygen attached to the quaternary carbon and methine carbon of epoxidized isoprene unit, respectively. The bands due to the C=S and C–O were clearly observed in the FTIR spectrum while the ¹H-NMR spectrum of the derivative revealed the peak attributed to the methylene protons had split. The ¹³C-NMR spectrum of the derivative further indicates two new carbon peaks arising from the >C=S and quaternary carbon of cyclic dithiocarbonate. All other ¹H- and ¹³C-NMR chemical shifts of the derivative remain unchanged with respect to the ENR-50.

The characterization of the effects of different sizes and loadings of Typha latifolia on the tensile, thermal, and morphological properties of linear-low-density polyethylene (LLDPE)/T. latifolia composites were evaluated using tensile test, Fourier transform infrared spectroscopy, thermogravimetric analysis, and scanning electron microscopy analyses. Results indicated the tensile strength and elongation at break decreased as T. latifolia loading increased. However, T. latifolia fine size (fs) exhibited better tensile properties than coarse size at the same loading in the composite. T. latifolia (15%, fs) recorded higher thermal stability than LLDPE control and other T. latifolia loadings and sizes due to the strong interaction of T. latifolia (15%, fs) in LLDPE matrix as shown in morphology.