The interactions of two ionic dyes, Crystal Violet and Methyl Orange, with different charged surfactants and also with a nonionic surfactant were investigated using surface tension measurements and visible spectroscopy in pre-micellar and post-micellar regions. It was found that for the water dominant phase systems the dye was localized between the polar heads, at the exterior of the direct micelle shells for all the systems. For the oil dominant phase systems, in case of the same charged dye/surfactant couples, the dye was localized in the micelle shell between the hydrocarbon chain of the surfactant nearby the hydrophilic head groups while for nonionic surfactant and oppositely charged dye/surfactant, localization of dye was between the oxyethylenic head groups towards the interior of the micelle core. Mixed aggregates of the dye and surfactant (below the critical micellar concentration of cationic surfactant), dye-surfactant ion pair and surfactant-micelles were present. The values of equilibrium constants (for TX-114/MO and TX-114/CV systems were 0.97 and 0.98, respectively), partition coefficients between the micellar and bulk water phases and standard free energy (for the nonionic systems were −12.59kJ/mol for MO and −10.97kJ/mol for CV) were calculated for all the studied systems. The partition processes were exothermic and occurred spontaneously

A new, clean, cost-effective and rapid method for the synthesis of stable spherical gold nanoparticles (AuNPs) is developed. This novel technique combines microemulsion as one of soft-nanotechnology techniques of wet chemistry, with photo-physics of UV-radiation in a unique versatile method to design and obtain controlled nanostructures for multifunctional materials. Based on a phase diagram in ternary water/Brij 30/ n -heptane system pristine, and thiol functionalized, gold nanoparticles were obtained by a microemulsion assisted photoreduction technique, allowing increased flexibility during the synthesis and selection of materials. The spherical nanoparticles obtained by this route show a homogeneous size distribution, with an average diameter of 11 nm, for pristine gold nanoparticles and of 12 nm, for functionalized species. The evolution of the system at the nanoscale has been studied using, in tandem, UV-VIS and DLS measurements. The structure, size and shape of the final nanoparticles obtained have been evaluated by adequate instrumental techniques: FTIR, XRD and TEM image analysis. Kinetic studies have also been performed in order to follow the evolution of nanospecies during irradiation procedure.