In this study, the liquid phase and vapor phase procedures for silylating cellulose microfibers by hexamethyldisilazane (HMDS) were compared in terms of efficiency. The influence of functionalization degree on the morphology of microfibers and their interaction with polydimethylsiloxane (PDMS) matrix has been investigated. The antibacterial properties of silylated cellulose microfibers hybridized with Ag nanoparticles, obtained by in situ chemical reduction, were also studied. Sample morphology investigations were carried out using spectroscopy and microscopy techniques (FTIR, XPS, TEM, SEM, EDS, XPS). Trimethylsilyl moieties appear on the surface of the cellulose microfibers after modification and improve the dispersibility of the microfibers, allowing strong interaction with the PDMS matrix and favoring its crosslinking density. Microfibers functionalized by the vapor phase of HMDS show smoother surfaces with higher concentrations of Si-containing groups, resulting in a more hydrophobic wetting behavior and a greater influence on the mechanical properties of the polymer. The silylated cellulose microfiber–Ag nanohybrid shows stronger antimicrobial activity towards Gram-positive and Gram-negative bacteria strains compared to that of the untreated hybrid. A PDMS composite loaded with this hybrid exhibits the ability to inhibit bacterial growth.

The most effective means to protect against bacterial invasion and to reduce the risk of healthcare-associated infections are antibacterial components synthesis. In this study, a novel process for the synthesis of organic–inorganic hybrid coatings containing silver nanoparticles is presented. Silver nanoparticles and polymer formation proceeds simultaneously through the in situ photoreduction of silver salt to silver nanoparticles and UV-crosslinking of bifunctional aliphatic silicone acrylate. The nanocomposite films with 0.5–1.43 wt % of silver nanoparticles concentration were obtained and investigated. The formation of silver nanoparticles in polymer matrix was confirmed via UV-visible spectroscopy, X-ray diffraction (XRD), Fourier transform infrared spectroscopy, scanning electron spectroscopy, and energy dispersive spectroscopy. Our investigations clearly show the formation of silver nanoparticles in silicone acrylate network. Direct photoreduction of silver salt by UV-radiation in the organic media produced silver nanoparticles exhibiting cubic crystal structure. The size of nanoparticles was determined to be near 20 ± 5 nm. The antibacterial activities of coatings were determined using the disc diffusion and direct contact methods. UV-curable silicone acrylate hybrid coatings exhibited antibacterial activity against harmful bacteria strains.