Phase changing materials (PCMs) microcapsules MPCM32D, consisting of a polymeric melamine-formaldehyde (MF) resin shell surrounding a paraffin core (melting point: 30–32 °C), have been modified by introducing thermally conductive additives on their outer shell surface. As additives, multiwall carbon nanotubes (MWCNTs) and poly (3,4-ethylenedioxyoxythiophene) poly (styrene sulphonate) (PEDOT: PSS) were used in different parts by weight (1 wt.%, 5 wt.%, and 10 wt.%). The main aim of this modification—to enhance the thermal performance of the microencapsulated PCMs intended for textile applications. The morphologic analysis of the newly formed coating of MWCNTs or PEDOT: PSS microcapsules shell was observed by SEM. The heat storage and release capacity were evaluated by changing microcapsules MPCM32D shell modification. In order to evaluate the influence of the modified MF outer shell on the thermal properties of paraffin PCM, a thermal conductivity coefficient (λ) of these unmodified and shell-modified microcapsules was also measured by the comparative method. Based on the identified optimal parameters of the thermal performance of the tested PCM microcapsules, a 3D warp-knitted spacer fabric from PET was treated with a composition containing 5 wt.% MWCNTs or 5 wt.% PEDOT: PSS shell-modified microcapsules MPCM32D and acrylic resin binder. To assess the dynamic thermal behaviour of the treated fabric samples, an IR heating source and IR camera were used. The fabric with 5 wt.% MWCNTs or 5 wt.% PEDOT: PSS in shell-modified paraffin microcapsules MPCM32D revealed much faster heating and significantly slower cooling compared to the fabric treated with the unmodified ones. The thermal conductivity of the investigated fabric samples with modified microcapsules MPCM32D has been improved in comparison to the fabric samples with unmodified ones. That confirms the positive influence of using thermally conductive enhancing additives for the heat transfer rate within the textile sample containing these modified paraffin PCM microcapsules.

The thermal properties of bio-based phase change material (PCM) microcapsules and their separate components, core and shell, were investigated considering the influence of used thermal enhancer. As a core, bio-based PCM, capric acid (CA), was used. Biodegradable material, such as polylactic acid (PLA), was used as a shell. To improve the thermal conductivity of PLA/CA microcapsules, the multiwall carbon nanotubes (MWCNTs) were used as a thermal enhancer. Composites of PCM with different concentrations of MWCNT as well as composites of PLA with these carbon compounds were prepared and investigated to assess how MWCNT influences the thermal conductivity of the core and the shell. The heat storage and release capacity, as well as the phase change temperatures of CA/MWCNT composites and manufactured PCM microcapsules, were determined using differential scanning calorimetry. To evaluate the thermal conductivity of prepared composites and to compare it with the conductivity of pure materials (without MWCNT), their thermal resistance was measured using the guarded-hotplate test method. To obtain the supplementary information and to assess the dynamic behavior of used PCM during the temperature changes, another technique, such as monitoring of a cold/hot plate with an IR camera, was used. The results of these measurements showed that introduced MWCNT increases the thermal conductivity of PCM used for the core and the conductivity of films prepared from PLA. Consequently, with reference to the results obtained, it could be stated that the introduction of MWCNT into PLA/CA microcapsules improved the thermal properties of these microcapsules. However, it was determined that too large concentration of MWCNT reduces an enthalpy of melting and crystallization of tested PCM and PCM microcapsules. Therefore, during the investigation, an optimal concentration of MWCNT additives has been determined.

The rapid growth of electronic devices, including wearable sensors, has increased electronic waste, driving interest in sustainable, biocompatible materials. Electrospun biomaterials have emerged as versatile substrates for multifunctional wearable textiles, offering flexibility, high surface area, tunable porosity, and biocompatibility. Using natural polymers (e.g., silk fibroin, cellulose, chitosan) and synthetic polymers (e.g., polycaprolactone, polylactic acid, PVDF), electrospinning produces nanofibrous mats capable of supporting thermal regulation, moisture management, and integrated sensing for pressure, temperature, humidity, or chemical detection. Nature-inspired designs, hybrid composites, and advanced architectures enable passive and active thermoregulation via phase-change materials, thermochromic dyes, hydrogels, and conductive nanofibers, while maintaining wearer comfort, breathability, and skin safety. Despite progress, challenges persist in durability, washability, energy efficiency, manufacturing scalability, and recyclability. This review provides a comprehensive overview of biomaterials, fabrication techniques, multifunctional sensor integration, and thermoregulation strategies, highlighting opportunities for next-generation wearable textiles that combine sustainability, adaptive thermal management, and high-performance sensing.

Wearing masks to protect against communicable diseases is an effective tool used in many countries affected by the COVID-19 pandemic. The antibacterial activity, antibacterial efficiency, microbial purity, and breathability properties of medical disposable masks are very important. Ag is most commonly applied to antimicrobial textiles. In this work, three antimicrobial additives were used. Four compositions of the binders with antimicrobial additives were prepared and applied to one-layer non-woven PP material. The influence of the binder antimicrobial polymer coating on the breathability and antibacterial activity of the non-woven PP material was evaluated. The results show that the composition of the polyacrylic acid binder had the least effect on their breathability and samples with the silver chloride formulation showed the best antimicrobial response. Based on the microbiological and air permeability results of the samples of the one-layer non-woven material with coating, the samples of two layers and three layers of the medical mask model were prepared. Microbiological studies have shown that a three-layered medical mask model with silver chloride composition in the middle layer, on both sides of the model, has antibacterial efficiency against three pathogens (E. Coli, K. Pneumoniae, and S. Aureus). The performance of this medical mask model has been found to meet the requirements for type I medical masks according to the EN 14863 standard. Studies have shown that the microbial purity of the mask model is CFU/g < 3.