Phase changing materials (PCMs) microcapsules MPCM32D, consisting of a polymeric melamine-formaldehyde (MF) resin shell surrounding a paraffin core (melting point: 30–32 °C), have been modified by introducing thermally conductive additives on their outer shell surface. As additives, multiwall carbon nanotubes (MWCNTs) and poly (3,4-ethylenedioxyoxythiophene) poly (styrene sulphonate) (PEDOT: PSS) were used in different parts by weight (1 wt.%, 5 wt.%, and 10 wt.%). The main aim of this modification—to enhance the thermal performance of the microencapsulated PCMs intended for textile applications. The morphologic analysis of the newly formed coating of MWCNTs or PEDOT: PSS microcapsules shell was observed by SEM. The heat storage and release capacity were evaluated by changing microcapsules MPCM32D shell modification. In order to evaluate the influence of the modified MF outer shell on the thermal properties of paraffin PCM, a thermal conductivity coefficient (λ) of these unmodified and shell-modified microcapsules was also measured by the comparative method. Based on the identified optimal parameters of the thermal performance of the tested PCM microcapsules, a 3D warp-knitted spacer fabric from PET was treated with a composition containing 5 wt.% MWCNTs or 5 wt.% PEDOT: PSS shell-modified microcapsules MPCM32D and acrylic resin binder. To assess the dynamic thermal behaviour of the treated fabric samples, an IR heating source and IR camera were used. The fabric with 5 wt.% MWCNTs or 5 wt.% PEDOT: PSS in shell-modified paraffin microcapsules MPCM32D revealed much faster heating and significantly slower cooling compared to the fabric treated with the unmodified ones. The thermal conductivity of the investigated fabric samples with modified microcapsules MPCM32D has been improved in comparison to the fabric samples with unmodified ones. That confirms the positive influence of using thermally conductive enhancing additives for the heat transfer rate within the textile sample containing these modified paraffin PCM microcapsules.

Regenerated cellulose fibers are a highly adaptable biomaterial with numerous medical applications owing to their inherent biocompatibility, biodegradability, and robust mechanical properties. In the domain of wound care, regenerated cellulose fibers facilitate a moist environment conducive to healing, minimize infection risk, and adapt to wound topographies, making it ideal for different types of dressings. In tissue engineering, cellulose scaffolds provide a matrix for cell attachment and proliferation, supporting the development of artificial skin, cartilage, and other tissues. Furthermore, regenerated cellulose fibers, used as absorbable sutures, degrade within the body, eliminating the need for removal and proving advantageous for internal suturing. The medical textile industry relies heavily on regenerated cellulose fibers because of their unique properties that make them suitable for various applications, including wound care, surgical garments, and diagnostic materials. Regenerated cellulose fibers are produced by dissolving cellulose from natural sources and reconstituting it into fiber form, which can be customized for specific medical uses. This paper will explore the various types, properties, and applications of regenerated cellulose fibers in medical contexts, alongside an examination of its manufacturing processes and technologies, as well as associated challenges.

This study presents the investigation of the electromagnetic properties and resistance performance of electrically conductive fabrics coated with composition containing the conjugated polymer system poly(3,4-ethylenedioxythiophene)-polystyrene sulfonate (PEDOT:PSS). The developed fabrics were intended for electromagnetic radiation (EMR) shielding in microwave range and for absorbing microwaves in radar operating range, so as to act as radar absorbing materials (RAM). The measurements of reflection and transmission of the developed fabrics were performed in a frequency range of 2–18 GHz, which covers the defined frequencies relevant to the application. Four types of fabrics with different fiber composition (polyamide; polyamide/cotton; wool and para-aramid/viscose) were selected and coated with conductive paste using screen printing method. It was found that EMR shielding effectiveness (SE) as well as absorption properties depend not only the amount of conductive paste topped on the fabric, but also resides in the construction parameters of fabrics. Depending on such fabric structural parameters as density, mass per unit area, type of weave, a layer of shield (or coating) just sticks on the fabric surface or penetrates into fabric, changing the shield thickness and herewith turning SE results. Meanwhile, the fiber composition of fabrics influences mostly bonding between fibers and polymer coating. To improve the resistance performance of the developed samples, a conventional textile surface modification technique, atmospheric plasma treatment, was applied. Initially, before plasma treatment and after treatment the fabrics were evaluated regarding an aqueous liquid repellency test, measuring the contact angles for the water solvent. The influence of plasma treatment on resistance performance of coated fabrics was evaluated by subjecting the plasma treated samples and untreated samples to abrasion in the Martindale abrasion apparatus and to multiplex washing cycles. These investigations revealed that applied plasma treatment visibly improved abrasion resistance as a result of better adhesion of the coating. However, washing resistance increased not so considerably.

The purpose of this study is to investigate the thermoregulatory properties of polyethylene terephthalate (PET) 3D knitted materials with bioceramic additives which are highly absorbing far-infrared (FIR) radiation. Ceramic materials are well-known and useful for thermal insulation applications. In order to compare different types of ceramic additives and coating methods for their incorporation into textile, several types of ceramic compounds with heat-retaining function were selected: germanium (Ge), aluminum (Al) and silicon (Si) additives were applied by impregnation in squeezing padder and titanium (Ti) by the screen printing method. The thermoregulatory properties (thermal resistance, heat-retaining effectiveness and air permeability) of 3D PET knits with bioceramic additives were estimated. In this study scanning electron microscopy (SEM) images were used to analyze the morphology of coated fabrics, X-ray fluorescence spectroscopy (XRF) analysis was applied to evaluate the number of minerals with high heat capacity in each formulation used for treatment. The knits coated with a formulation containing Ti ceramic additives demonstrated the most effective thermal behavior. Furthermore, better heat accumulation effectiveness of Ti ceramics containing knits was confirmed by Fourier transform infrared spectroscopy (FTIR) analysis. It was also determined that 3D knitted fabric with Ti ceramic additives showed the highest emissivity among tested samples and the implication is that this sample radiates its energy more efficiently than others.

The influence of different concentrations of salt-added polyethylene oxide (PEO) on the spinnability of chitosan (CS)/PEO + NaCl blends that could be used as a component part of filters for water treatment or nanofiber membranes as well as for medical applications was investigated in this study. The morphological properties of manufactured nanofibers were analyzed as well. It was determined that an increase of PEO concentration resulted mostly in thin and round nanofibers formed during electrospinning, but the manufacturing process became complex, because many wet fibers reached the collector while spinning. Also, it was noticed that the salt was not dissolved completely in the polymer solutions and some crystals were seen in the SEM images of manufactured fiber mats. However, the addition of salt resulted in lower viscosity and better conductivity of solution and fiber mats as well. The opposite effect was observed as the concentration of PEO was increased. The orientation of produced nanofibers as well as their diameter were analyzed with commercially available software. It was determined that the results obtained by software and microscopically are repeatable. The difference among the results of diameter calculated with software and taken by microscope varied from 0% to approximately 12%. The FTIR analyses indicated that alterations in polymer concentrations or the addition of salt did not induce any discernible changes in the chemical composition or nature of the materials under investigation. The sodium chloride present in the solutions enhanced electrical properties and increased conductivity values more than 50 times for PEO solutions and six times for CS/PEO blend solutions, compared to conductivity values of solutions without salt. To assess the thermal characteristics of the PEO/CS blend nanofibers, measurements using a differential scanning calorimeter (DSC) to determine melting (Tm) and crystallization (Tc) temperatures, as well as specific heat capacities were conducted. These parameters were derived from the analysis of endothermic and exothermic peaks observed in the DSC data. It showed that all produced nanofibers were semicrystalline.

The increasing interest in developing biodegradable polymers through chemical treatments, microorganisms, and enzymes highlights a commitment to environmentally friendly disposal methods