Biocompatibility is important for the 3D printing of resins used in medical devices and can be affected by photoinitiators, one of the key additives used in the 3D printing process. The choice of ingredients must be considered, as the toxicity varies depending on the photoinitiator, and unreacted photoinitiator may leach out of the polymerized resin. In this study, the use of ethyl (2,4,6-trimethylbenzoyl) phenylphosphinate (TPO-L) as a photoinitiator for the 3D printing of resin was considered for application in medical device production, where the cytotoxicity, colour stability, dimensional accuracy, degree of conversion, and mechanical/physical properties were evaluated. Along with TPO-L, two conventional photoinitiators, phenylbis (2,4,6-trimethylbenzoyl) phosphine oxide (BAPO) and diphenyl (2,4,6-trimethylbenzoyl) phosphine oxide (TPO), were considered. A total of 0.1 mol% of each photoinitiator was mixed with the resin matrix to prepare a resin mixture for 3D printing. The specimens were printed using a direct light processing (DLP) type 3D printer. The 3D-printed specimens were postprocessed and evaluated for cytotoxicity, colour stability, dimensional accuracy, degree of conversion, and mechanical properties in accordance with international standards and the methods described in previous studies. The TPO-L photoinitiator showed excellent biocompatibility and colour stability and possessed with an acceptable dimensional accuracy for use in the 3D printing of resins. Therefore, the TPO-L photoinitiator can be sufficiently used as a photoinitiator for dental 3D-printed resin.

The aim of this study is to investigate the resistance of various fluoride-releasing restorative materials against the demineralization and remineralization of enamel surfaces, including those that have been recently introduced to the market. Three different fluoride-releasing restorative materials were considered: glass ionomer (FI), resin-modified glass ionomer (RL), and an alkasite restorative material (CN). The acid neutralization ability was investigated using pH measurement, and the concentrations of released fluoride and calcium ions were measured. Finally, the demineralization resistance and remineralization effects of enamel were observed using a microhardness tester and SEM. CN showed an initial substantial increase in pH followed by a steady increase, with values higher than those of the other groups (p < 0.05). All three groups released fluoride ions, and the CN group released more calcium ions than the other groups (p < 0.05). In the acid resistance test, from the microhardness and SEM images, the CN group showed effective resistance to demineralization. In the remineralization test, the microhardness results showed that the FI and CN groups recovered the microhardness from the values of the demineralized enamel surface (p < 0.05). This was confirmed by the SEM images from remineralization tests; the CN group showed a recovered demineralized surface when immersed in artificial saliva for 7 days. In conclusion, alkasite restorative material can be an effective material when used in cariogenic environments.

The objective of this study was to investigate the effects of hydrated calcium silicate filler (hCS) on resin-based pit and fissure sealants’ acid neutralization, calcium ion release, and mechanical and physical properties. To produce the hCS filler, Portland cement (CS) was mixed with distilled water and ground into fine particles. The particles were then mixed with silanized glass filler and added to a photo-activated resin matrix. To evaluate the acid neutralization and calcium ion release properties, the specimens were immersed in a pH 4.0 lactic acid solution and distilled water for 28 days. Also, the flexural strength, depth of cure, water sorption, and solubility were tested. All of the groups containing hCS and CS required less than one minute to increase the pH from 4.0 to 5.5. With 50% hCS, the calcium ion release was higher than 50% CS in the distilled water at the initial time. The flexural strength and depth of cure decreased according to the increasing proportion of hCS added. The water sorption and solubility had an increasing trend as increasing proportions of hCS were added. These findings showed that pit and fissure sealant containing hCS exhibit superior acid neutralization and calcium release properties, and may be promising for caries-inhibiting dental material.

The objective of the study was to compare the acid neutralizing ability and shear bond strength (SBS) of three different types of orthodontic adhesives containing bioactive glasses (BAGs). 45S5, 45S5F and S53P4 BAGs were prepared using the melting technique and ground to fine particles. Orthodontic adhesives containing three types of BAGs were prepared as follows: 52.5% 45S5 BAG + 17.5% glass (45S5_A); 61.25% 45S5 BAG + 8.75% glass (45S5_B); 52.5% 45S5F BAG + 17.5% glass (45S5F_A); 61.25% 45S5F BAG + 8.75% glass (45S5F_B); 52.5% S53P4 BAG + 17.5% glass (S53P4_A); 61.25% S53P4 BAG + 8.75% glass (S53P4_B); and 70.0% glass (BAG_0). To evaluate the acid neutralizing properties, specimens were immersed in lactic acid solution, and pH changes were measured. SBS was measured with a universal testing machine. For all of the BAG-containing adhesives, the one with 61.25% of BAG showed a significantly greater increase of pH than the one with 52.5% of BAG (p < 0.05). Groups with 61.25% of BAG showed lower SBS than samples with 52.5% of BAG. 45S5F_A showed no significant difference of SBS compared to BAG_0 (p > 0.05). The adhesive containing 61.25% of 45S5F BAG exhibited clinically acceptable SBS and acid neutralizing properties. Therefore, this composition is a suitable candidate to prevent white spot lesions during orthodontic treatment.

Various materials have been introduced for the three-dimensional (3D) printing of dentures. In this study, the color stability and surface and physicochemical properties of 3D-printed denture base resins with four types of nanofiller particles were evaluated. Al₂O₃, ZnO, CeZr, and SiO₂ nanofillers were added to a 3D printable denture base-resin matrix and subjected to digital light processing. The specimens were immersed in Coke, coffee, black tea, or distilled water for 6 days. For the assessment of color differences, 6 samples were analyzed using a spectrophotometer. In a separate investigation, surface properties of 10 samples were examined, while a different set of 6 samples was used to analyze water sorption and solubility. All experimental groups exhibited higher color stability in Coke than the control group. However, the groups containing ZnO and CeZr had lower color stability in coffee and black tea than the control group. Moreover, they had agglomerated nanofillers and lower gloss than the control group. Compared with that of the control group, the contact angle of the CeZr group and microhardness of the ZnO group were not significantly different. Water sorption was higher in the Al₂O₃ group, whereas the solubility of the experimental and control groups was not statistically significant. The results demonstrated the significant effect of ZnO and CeZr nanofillers on the color stability of the dentures when exposed to discoloring beverages. These results will facilitate the development of fillers that enhance the resistance of 3D printed denture base resins to discoloration in the oral environment.

We aimed to evaluate the antimicrobial effects of Glycyrrhiza uralensis extract on Streptococcus mutans and Candida albicans and its biocompatibility for dental applications. The antimicrobial activity of the G. uralensis extracts at concentrations of 50, 100, 150, and 200 µg/mL was assessed using agar disk diffusion tests, counting the total number of colony-forming units (CFUs), spectrophotometric growth inhibitory assays, and microbial morphology observations using scanning electron microscopy (SEM; Merin, Carl Zeiss, Oberkochen, Germany). We measured the polyphenol and flavonoid contents of G. uralensis extracts using ultraviolet–visible spectrometry and the cytotoxicity of these extracts using an MTT (3-(4,5-Dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide) assay. We identified that G. uralensis extracts had significant antimicrobial effects against S. mutans and C. albicans. The optical density of the experimental groups significantly decreased compared with that of the control group. SEM images revealed that the G. uralensis extract affected the morphology and density of S. mutans and C. albicans. The extract concentration of flavonoids, but not polyphenols, increased with increasing concentrations of the G. uralensis extract. Furthermore, cell viabilities were more than 70% for G. uralensis extracts with concentrations of 50 and 100 μg/mL. Naturally derived G. uralensis is biocompatible and exhibits an excellent antimicrobial effect against oral pathogens such as S. mutans and C. albicans. Thus, G. uralensis extracts can be used for the development of oral products that treat and prevent oral diseases.