Magnesium and its alloys have become potential implant materials in the future because of light weight, mechanical properties similar to natural bone, good biocompatibility, and degradability in physiological environment. However, due to the rapid corrosion and degradation of magnesium alloys in vivo, especially in the environment containing chloride ions, the application of magnesium alloys as implant materials has been limited. Therefore, improving the corrosion resistance of magnesium alloy and ensuring good biocompatibility is the main focus of the current research. In this study, hydroxyapatite coating was prepared on magnesium alloy surface using carboxymethyl cellulose-dopamine hydrogel as inducer to improve corrosion resistance and biocompatibility. Surface characterization techniques (scanning electron microscopy, Fourier-transformed infrared spectroscopy, energy dispersive X-ray spectroscopy- and X-ray diffraction) confirmed the formation of hydroxyapatite on the surface of AZ31 alloy. Corrosion resistance tests have proved the protective effect of Carboxymethyl cellulose-Dopamine/hydroxyapatite (CMC-DA/HA) coating on the surface of AZ31 alloy. According to MC3T3-E1 cell viability and Live/Dead staining, the coating also showed good biocompatibility. The results will provide new ideas for the biological application of magnesium alloys.

In this study, films with different fluorine contents were prepared on an AZ31 magnesium alloy by using plasma electrolytic oxidation to study the corrosion resistance and cytocompatibility of the alloy. The morphology of the coating surface, phase, and chemical elements were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), and energy-dispersive X-ray spectrometry (EDS). The changes in the corrosion resistance with different fluorine contents were investigated by electrochemical experiments, hydrogen evolution, and long-term immersion tests. In addition, murine fibroblast L-929 cells were adopted for in vitro cytotoxicity tests using the cell counting kit (CCK)-8 assay, and the morphology of the cells was observed simultaneously by inverted microscopy. The results showed that the main form of the fluorine ions in the plasma electrolytic oxidation coatings was magnesium fluoride (MgF₂). In addition, the corrosion resistance and cytocompatibilities of the coatings were improved by the addition of fluoride ions. When the content of potassium fluoride reached 10 g/L, the cell compatibility and corrosion resistance were the best, a finding which provides a basis for the clinical applications of the AZ31 magnesium alloy in the biomedical field.

The objectives of this study were to reduce the corrosion rate and increase the cytocompatibility of AZ31 Mg alloy. Two coatings were considered. One coating contained MgO (MAO/AZ31). The other coating contained Cu²⁺ (Cu/MAO/AZ31), and it was produced on the AZ31 Mg alloy via microarc oxidation (MAO). Coating characterization was conducted using a set of methods, including scanning electron microscopy, energy-dispersive spectrometry, X-ray photoelectron spectroscopy, and X-ray diffraction. Corrosion properties were investigated through an electrochemical test, and a H₂ evolution measurement. The AZ31 Mg alloy with the Cu²⁺-containing coating showed an improved and more stable corrosion resistance compared with the MgO-containing coating and AZ31 Mg alloy specimen. Cell morphology observation and cytotoxicity test via Cell Counting Kit-8 assay showed that the Cu²⁺-containing coating enhanced the proliferation of L-929 cells and did not induce a toxic effect, thus resulting in excellent cytocompatibility and biological activity. In summary, adding Cu ions to MAO coating improved the corrosion resistance and cytocompatibility of the coating.