The scope of silicone rubber (SiR) is confined due to the deprivation of its dielectric propertiesupon exposure to various ambient stresses. The aim of this research is to develop silicone rubber-based composites by employing inorganic oxide fillers for improved dielectric and high voltage insulation properties for widening its scope in the field of electrical appliances. This study reports the preparation of different composites of silicone rubber with varying concentrations of micro and nano-silica fillers. The dielectric propertytrends of these as-prepared neat and impregnated samples were examined via an indigenously developed weathering chamber capable of applying multiple stresses of acid rain, heat, humidity, UVA radiation, and salt fog. Dielectric constant values were measured before and after applying stresses. Upon applying stresses, a periodic decline in dielectric constant was observed. Improved dielectric properties were obtained by adding micro and nano-silica as fillers. A nano silica-incorporated silicone rubber product exhibited good potential for dual applications as dielectric and high voltage insulation.

Degradation of silicon rubber due to heat and humidity affect its performance in outdoor applications. To analyze the effects of high temperature and humidity on room temperature vulcanized (RTV) silicone rubber (SiR) and its composites, this study was performed. Five different sample compositions including neat silicone rubber (nSiR), microcomposites (15 wt% silica(SMC 15% SiO₂) and 15 wt% ATH(SMC 15% ATH), nanocomposite (2.5 wt% silica(SNC 2.5% SiO₂) and hybrid composite (10 wt% micro alumina trihydrate with 2 wt% nano silica(SMNC 10% ATH 2% SiO₂) were prepared and subjected to 70 ˚C temperature and 80% relative humidity in an environmental chamber for 120 h. Contact angle, optical microscopy and Fourier transform infrared (FTIR) spectroscopy were employed to analyze the recovery properties before and after applying stresses. Different trends of degradation and recovery were observed for different concentrations of composites. Addition of fillers improved the overall performance of composites and SMC 15% ATH composite performed better than other composites. For high temperature and humidity, the ATH-based microcomposite was recommended over silica due to its superior thermal retardation properties of ATH. It has been proved that ATH filler is able to withstand high temperature and humidity.