This study evaluated the effect of hypertension on tissue response and biomineralization capacity of white Mineral Trioxide Aggregate (MTA), High-plasticity MTA (MTA HP), and Biodentine® (BDT) in rats. Polyethylene tubes filled with MTA, MTA HP, BDT, and the control group (empty tubes) were placed into the dorsal subcutaneous tissue of 32 male rats (16 normotensive (NT) and 16 hypertensive rats - 8 per group). After 7 and 30 days, the polyethylene tubes surrounded by connective tissue were removed, fixed, and embedded in histological resin. The mean number of inflammatory cells was estimated in HE-stained sections, biomineralization was quantified as area (µm2) by Kossa (VK) staining, and examination by polarized light (LP) microscopy was performed. The differences amongst the groups were analyzed statistically by the Mann-Whitney or Student's t test, according to Shapiro-Wilk test of normality (p < 0.05). The inflammatory responses to all materials were greater in hypertensive rats than in NT rats (p < 0.05). Positive VK staining in MTA and BDT were more pronounced in NT rats at 7 and 30 days (p < 0.05). Birefringent structures in LP for MTA, MTA HP, and BDT were more pronounced in NT rats at 7 days (p<0.05). In rats, hypertension was able to increase inflammatory infiltrate and decrease biomineralization of the tested materials.

To evaluate the cytotoxicity, biocompatibility and mineralization capacity of BIO-C PULPO, and MTA. L929 fibroblasts were cultured and MTT assay was used to determine the material cytotoxicity on 6, 24, and 48 h. A total of 30 male rats (Wistar) aged between 4 and 6 months, weighing between 250 and 300 g were used. Polyethylene tubes containing BIO-C PULPO, MTA, and empty tubes were implanted into dorsal connective tissue. After the experimental periods (7, 15, 30, 60, and 90 days) the tubes were histologically analyzed using hematoxylin-eosin (H&E), immunolabeling of IL-1β and TNF-α, and von Kossa staining, or without staining for polarized light analysis. The average number of inflammatory cells was quantified; the mineralization assessment was determined by the area marked in μm2 and semiquantitative immunolabeling analyses of IL-1β and TNF-α were performed. Then, data underwent statistical analysis with a 5% significance level. It was observed that BIO-C PULPO and MTA presented cytocompatibility at 6, 24, and 48 similar or higher than control for all evaluated period. On periods 7 and 15 days, BIO-C PULPO was the material with the highest number of inflammatory cells (p0.05). No statistical differences were found between Control, BIO-C PULPO, and MTA for immunolabeling of IL-1β and TNF-α in the different periods of analysis (p<0.05). Positive von Kossa staining and birefringent structures under polarized light were observed in all analyzed periods in contact with both materials, but larger mineralization area was found with BIO-C PULPO on day 90 (p<0.05). BIO-C PULPO was biocompatible and induced mineralization similar to MTA.