New mineral trioxide aggregate (MTA) formulations are constantly introduced in the market, usually in a powder-and-liquid form. Bioceramic (Bio-C) Repair is a ready-for-use material suggested as substitute for MTA, but its properties need to be studied. This study evaluated the cytotoxicity, biocompatibility and biomineralization of Bio-C Repair compared to MTA Repair High-Plasticity (MTA-HP) and white MTA-Angelus (MTA-Ang). L929 fibroblasts were exposed to material-extracted (undiluted, ½ and ¼ dilutions; 6, 24 and 48h). Polyethylene tubes with material or empty (control) were implanted in the subcutaneous tissue of rats. After 7 and 30 days (n=8), the specimens were removed for analysis (hematoxylin-eosin, von Kossa and polarized light). Cytotoxicity data were statistically analyzed by two-way ANOVA, and biocompatibility data by Kruskal-Wallis and Dunn tests (p<0.05). The cells exposed to the materials had greater viability at most of the periods compared with control (p<0.05). The undiluted and ½ dilutions of MTA-HP extract showed higher cytocompatibility than Bio-C Repair at 6 h and with the ¼ dilution at 24 h (p<0.05); the white MTA-Ang showed higher cytocompatibility than Bio-C Repair at most of periods (p<0.05). The undiluted white MTA-Ang extract had higher cytocompatibility at 6 and 24h than MTA-HP, and with ½ dilution at 24h (p0.05). At 7 and 30 days, the groups had moderate and mild inflammation, respectively (p>0.05). All materials showed positive structures for von Kossa and polarized light. In conclusion, Bio-C Repair had similar cytocompatibility to MTA-based materials is biocompatible and induces biomineralization.

This study evaluated the cytotoxicity and biocompatibility of a new bioceramic endodontic sealer (i.e., Sealer Plus BC) in comparison with those of MTA Fillapex and AH Plus. L929 fibroblasts were cultured and Alamar Blue was used to evaluate cell viability of diluted extracts (1:50, 1:100, and 1:200) from each sealer at 24 h. Polyethylene tubes that were filled with material or empty (as a control) were implanted in the subcutaneous tissue of rats. The rats were killed after 7 and 30 d (n = 8), and the tubes were removed for histological analysis. Parametric data was analyzed using a one-way ANOVA test, and nonparametric data was analyzed via the Kruskal–Wallis test followed by the Dunn test (p < 0.05). A reduction in cell viability was observed in the extracts that were more diluted for Sealer Plus BC when compared to that of Control and AH Plus (p < 0.05). However, the 1:50 dilution of the Sealer Plus BC was similar to that of the Control (p > 0.05). Conversely, more diluted extracts of MTA Fillapex (1:200) and AH Plus (1:100 and 1:200) were similar to the Control (p > 0.05). Histological analysis performed at 7 d did not indicate any significant difference between tissue response for all materials, and the fibrous capsule was thick (p > 0.05). At 30 d, Sealer Plus BC was similar to the Control (p > 0.05) and MTA Fillapex and AH Plus exhibited greater inflammation than the Control (p < 0.05). The fibrous capsule was thin for the Control and for most specimens of Sealer Plus BC and AH Plus. Thus, Sealer Plus BC is biocompatible when compared to MTA Fillapex and AH Plus, and it is less cytotoxic when less-diluted extracts are used.