Microplastics (MPs) are distributed in a wide range of aquatic and terrestrial ecosystems throughout the planet. They are known to adsorb hazardous substances and can transfer them across the trophic web. To eliminate MPs pollution in an environmentally friendly process, we propose using a photocatalytic process that can easily be implemented in wastewater treatment plants (WWTPs). As photocatalysis involves the formation of reactive species such as holes (h⁺), electrons (e⁻), hydroxyl (OH^●), and superoxide ion (O₂^●−) radicals, it is imperative to determine the role of those species in the degradation process to design an effective photocatalytic system. However, for MPs, this information is limited in the literature. Therefore, we present such reactive species’ role in the degradation of high-density polyethylene (HDPE) MPs using C,N-TiO₂. Tert-butanol, isopropyl alcohol (IPA), Tiron, and Cu(NO₃)₂ were confirmed as adequate OH^●, h⁺, O₂^●− and e⁻ scavengers. These results revealed for the first time that the formation of free OH^● through the pathways involving the photogenerated e⁻ plays an essential role in the MPs’ degradation. Furthermore, the degradation behaviors observed when h⁺ and O₂^●− were removed from the reaction system suggest that these species can also perform the initiating step of degradation.

Microplastics (MPs) are plastic particles with sizes between 1 μm and 5 mm with a ubiquitous presence in aquatic ecosystems. MPs harm marine life and can cause severe health problems for humans. Advanced oxidation processes (AOPs) that involve the in-situ generation of highly oxidant hydroxyl radicals can be an alternative to fight MPs pollution. Of all the AOPs, photocatalysis has been proven a clean technology to overcome microplastic pollution. This work proposes novel C,N-TiO₂/SiO₂ photocatalysts with proper visible-active properties to degrade polyethylene terephthalate (PET) MPs. Photocatalysis was performed in an aqueous medium and at room temperature, evaluating the influence of two pH values (pH 6 and 8). The results demonstrated that the degradation of the PET MPs by C,N-TiO₂/SiO₂ semiconductors is possible, achieving mass losses between 9.35 and 16.22 %.

Pac-Man TiO₂ particles exhibit excellent photocatalytic properties. Degradation of highly reactive H₂O₂ leads to microscale propulsion, and the reactive oxygen species enable dye and polymer decomposition, even though at much slower time scales.

The aim of this research was to evaluate the possibility of reusing waste foundry sands derived from the production of cast iron as a secondary raw material for the production of building materials obtained both by high-temperature (ceramic tiles and bricks) and room-temperature (binders such as geopolymers) consolidation. This approach can reduce the current demand for quarry sand and/or aluminosilicate precursors from the construction materials industries. Samples for porcelain stoneware and bricks were produced, replacing the standard sand contained in the mixtures with waste foundry sand in percentages of 10%, 50%, and 100% by weight. For geopolymers, the sand was used as a substitution for metakaolin (30, 50, 70 wt%) as an aluminosilicate precursor rather than as an aggregate to obtain geopolymer pastes. Ceramic samples obtained using waste foundry sand were characterized by tests for linear shrinkage, water absorption, and colorimetry. Geopolymers formulations, produced with a Si/Al ratio of 1.8 and Na/Al = 1, were characterized to evaluate their chemical stability through measurements of pH and ionic conductivity, integrity in water, compressive strength, and microstructural analysis. The results show that the addition of foundry sand up to 50% did not significantly affect the chemical-physical properties of the ceramic materials. However, for geopolymers, acceptable levels of chemical stability and mechanical strength were only achieved when using samples made with 30% foundry sand as a replacement for metakaolin.

Microplastics (MPs) and nanoplastics (NPs) are distributed and transferred among the four major environmental compartments (air, water, soil, and biota) and have been already found in humans, making crucial to develop remediation technologies to tackle this kind pollution. Photocatalysis can be used to eliminate MPs present in contaminated wastewater effluents before their discharge into waterbodies. In this work, several green TiO2-based semiconductors were prepared using the extrapallial fluid (EPF) of Mytilus edulis sea water mussels as doping precursor. The semiconductors were then used as films or powders to photocatalytically degrade polystyrene (PS) NPs and MPs and polyethylene (PE) MPs. It was found that the obtention of green TiO2-based semiconductors with good characteristics for photocatalytic purposes (anatase crystalline phase, presence of porosity, activity in visible light and high surface area) seems not enough to achieve high degradation efficiency. The operational conditions of the reaction system should be also taken into account. For instance, the convenience of using semiconductors in the form of films can be overcome by their limited exposed surface area or the null adsorption of the semiconductor in the MPs particles. Additionally, crystallinity of the semiconductor can be a more determinant factor to take into account when performing photocatalysis of MPs.