The aim of this research was to evaluate the possibility of reusing waste foundry sands derived from the production of cast iron as a secondary raw material for the production of building materials obtained both by high-temperature (ceramic tiles and bricks) and room-temperature (binders such as geopolymers) consolidation. This approach can reduce the current demand for quarry sand and/or aluminosilicate precursors from the construction materials industries. Samples for porcelain stoneware and bricks were produced, replacing the standard sand contained in the mixtures with waste foundry sand in percentages of 10%, 50%, and 100% by weight. For geopolymers, the sand was used as a substitution for metakaolin (30, 50, 70 wt%) as an aluminosilicate precursor rather than as an aggregate to obtain geopolymer pastes. Ceramic samples obtained using waste foundry sand were characterized by tests for linear shrinkage, water absorption, and colorimetry. Geopolymers formulations, produced with a Si/Al ratio of 1.8 and Na/Al = 1, were characterized to evaluate their chemical stability through measurements of pH and ionic conductivity, integrity in water, compressive strength, and microstructural analysis. The results show that the addition of foundry sand up to 50% did not significantly affect the chemical-physical properties of the ceramic materials. However, for geopolymers, acceptable levels of chemical stability and mechanical strength were only achieved when using samples made with 30% foundry sand as a replacement for metakaolin.

A new method for fast and simple synthesis of crystalline TiO₂ nanoparticles with photocatalytic activity was developed by carrying out a classic sol–gel reaction directly under vacuum. The use of microwaves for fast heating of the reaction medium further reduces synthesis times. When the solvent is completely removed by vacuum, the product is obtained in the form of a powder that can be easily redispersed in water to yield a stable nanoparticle suspension, exhibiting a comparable photocatalytic activity with respect to a commercial product. The present methodology can, therefore, be considered a process intensification procedure for the production of nanotitania.